Liquid crystalline medium

ABSTRACT

The present invention relates to a liquid crystalline mixture comprising 
 
a) 1-25% by weight of at least one compound of the formula I  
                 
 
b) 5-80% by weight of at least one compound of the formula II  
                 
c) and optionally 1-20% by weight of at least one chiral compound with a HTP of ≦20 μm, wherein 
 
R 11 , A 11 , Z 11 , A 12 , Z 12 , L 11 , L 12 , L 13 , L 14 , Z 13 , A 13 , Z 14 , A 14 , X 11 , a, b, c, d, R 12 , A 1 , Z 1 ,  
                 
 
A 2 , Z 2 , A 3 , L 1 , L 2 , X 12 , m and n have the meanings given in claim  1  and their use in TFT, TN, IPS applications and expecially for devices utilizing electro-optical effects in an optically isotropic state.

The present invention is related to a liquid crystal medium and the use of said media in electro-optical devices, and especially for the use in electro-optical devices that may be operated in an optically isotropic state.

Liquid crystals are used generally as dielectrics in display devices, since the optical properties of such substances can be modified by an applied voltage. Electro-optical devices based on liquid crystals are extremely well known to the person skilled in the art and can be based on various effects. Examples of such devices are cells having dynamic scattering, DAP (deformation of aligned phases) cells, guest/host cells, TN cells having a twisted nematic structure, STN (supertwisted nematic) cells, SBE (super-birefringence effect) cells and OMI (optical mode interference) cells. The most common display devices are based on the Schadt-Helfrich effect and have a twisted nematic structure.

The liquid crystal materials must have good chemical and thermal stability and good stability to electric fields and electromagnetic radiation. Furthermore, the liquid crystal materials should have low viscosity and produce short addressing times, low threshold voltages and high contrast in the cells.

They should furthermore have a suitable mesophase, for example a nematic or cholesteric mesophase for the above-mentioned cells, at the usual operating temperatures, i.e. in the broadest possible range above and below room temperature. Since liquid crystals are generally used as mixtures of a plurality of components, it is important that the components are readily miscible with one another. Further properties, such as the electrical conductivity, the dielectric anisotropy and the optical anisotropy, have to satisfy various requirements depending on the cell type and area of application. For example, materials for cells having a twisted nematic structure should have positive dielectric anisotropy and low electrical conductivity.

For example, for matrix liquid crystal displays with integrated non-linear elements for switching individual pixels (MLC displays), media having large positive dielectric anisotropy, broad nematic phases, relatively low birefringence, very high specific resistance, good UV and temperature stability and low vapour pressure are desired.

Matrix liquid crystal displays of this type are known. Non-linear elements which can be used for individual switching of the individual pixels are, for example, active elements (i.e. transistors). The term “active matrix” is then used, where a distinction can be made between two types:

-   1. MOS (metal oxide semiconductor) or other diodes on a silicon     wafer as substrate. -   2. Thin-film transistors (TFTs) on a glass plate as substrate.

The use of single-crystal silicon as substrate material restricts the display size, since even modular assembly of various part-displays results in problems at the joins.

In the case of the more promising type 2, which is preferred, the electro-optical effect used is usually the TN effect. A distinction is made between two technologies: TFTs comprising compound semiconductors, such as, for example, CdSe, or TFTs based on polycrystalline or amorphous silicon. Intensive work is being carried out world-wide on the latter technology.

The TFT matrix is applied to the inside of one glass plate of the display, while the other glass plate carries the transparent counterelectrode on its inside. Compared with the size of the pixel electrode, the TFT is very small and has virtually no adverse effect on the image. This technology can also be extended to fully colour-capable displays, in which a mosaic of red, green and blue filters is arranged in such a way that a filter element is opposite each switchable pixel.

The TFT displays usually operate as TN cells with crossed polarisers in transmission and are illuminated from the back.

The term MLC displays here covers any matrix display with integrated non-linear elements, i.e., besides the active matrix, also displays with passive elements, such as varistors or diodes (e.g. MIM diodes=metal-insulator-metal).

MLC displays of this type are particularly suitable for TV applications (for example pocket TVs) or for high-information displays for computer applications (laptops) and in automobile or aircraft construction. Besides problems regarding the angle dependence of the contrast and the response times, difficulties also arise in MLC displays due to insufficiently high specific resistance of the liquid crystal mixtures [TOGASHI, S., SEKIGUCHI, K., TANABE, H., YAMAMOTO, E., SORIMACHI, K., TAJIMA, E., WATANABE, H., SHIMIZU, H., Proc. Eurodisplay 84, September 1984: A 210-288 Matrix LCD Controlled by Double Stage Diode Rings, p. 141 ff, Paris; STROMER, M., Proc. Eurodisplay 84, September 1984: Design of Thin Film Transistors for Matrix Addressing of Television Liquid Crystal Displays, p. 145 ff, Paris]. With decreasing resistance, the contrast of an MLC display deteriorates, and the problem of after-image elimination may occur. Since the specific resistance of the liquid crystal mixture generally drops over the life of an MLC display owing to interaction with the interior surfaces of the display, a high (initial) resistance is very important in order to obtain acceptable service lives. In particular in the case of low-volt mixtures, it was hitherto impossible to achieve very high specific resistance values. It is furthermore important that the specific resistance exhibits the smallest possible increase with increasing temperature and after heating and/or UV exposure. The low-temperature properties of the mixtures from the prior art are also particularly disadvantageous. It is demanded that no crystallisation and/or smectic phases occur, even at low temperatures. Furthermore, in order to achieve an appropriate image quality high values of the voltage holding ratio (VHR) as well as a low dependence on temperature of the VHR are required. (The VHR reflects the decrease of a voltage applied to a display pixel as a function of time; a high VHR value indicates an only slight decrease of the voltage applied.) The MLC displays from the prior art thus do not meet today's requirements.

There thus continues to be a great demand for MLC displays having very high specific resistance at the same time as a large working-temperature range, short response times even at low temperatures, low threshold voltage, high VHR values with a low temperature dependence which do not have these disadvantages, or only do so to a lesser extent.

In TN (Schadt-Helfrich) cells, media are desired which facilitate the following advantages in the cells:

-   extended nematic phase range (in particular down to low     temperatures) -   the ability to switch at extremely low temperatures (outdoor use,     automobile, avionics) -   increased resistance to UV radiation (longer service life) -   high Δ∈ for low threshold voltages.

The mixture for the isotrop switching made are desired which facilitate the following advantages in the cells:

-   low operating voltage -   broad operating temperature range -   large voltage holding ratio

The media available from the prior art do not allow these advantages to be achieved while simultaneously retaining the other parameters.

In the case of supertwisted (STN) cells, media are desired which enable greater multiplexability and/or lower threshold voltages and/or broader nematic phase ranges (in particular at low temperatures). To this end, a further widening of the available parameter latitude (clearing point, smectic-nematic transition or melting point, viscosity, dielectric parameters, elastic parameters) is urgently desired. This applies as well to in-plane switching (IPS) cells, where the electrical field in the cell is not vertically aligned, like in TN or STN cells, but horizontally aligned.

It is therefore an object of the present invention to a liquid crystal media which do not have the above-mentioned disadvantages or only to a reduced extent and which preferably provides said media with advantageous properties such as low threshold voltages, high values of VHR and low temperature dependence of the operating voltage.

It has now been found that this object surprisingly can be achieved by the liquid crystalline medium according to the present invention.

The present invention relates to a liquid crystalline mixture consisting of

-   a) 1-25% by weight of a component A containing at least one compound     of the formula I     wherein -   a, b, c and d are each independently of each other 0, 1 or 2,     whereby a+b+c+d≦4; -   R¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms,     wherein one or more methylene groups of said alkyl or alkoxy radical     may be replaced independently of each other by —O—, —S—,     —SiR^(x)R^(y)—, —CH═CH—, —C≡C—, —CO—O— and/or —O—CO— such that     oxygen and/or sulfur atoms are not linked directly to each. other,     said alkyl or alkoxy radical being unsubstituted or mono-substituted     with a —CN group or mono- or poly-substituted with halogen; -   L¹¹, L¹², L¹³ and L⁴ are each independently of each other hydrogen,     halogen, a CN group, an alkyl or alkoxy radical having from 1 to 15     carbon atoms wherein one or more methylene groups of said alkyl or     alkoxy radical may be replaced independently of each other by —O—,     —S—, —SiR^(x)R^(y)—, —CH═CH—, —C≡C—, —CO—O— and/or —O—CO— such that     oxygen and/or sulfur atoms are not linked directly to each other,     said alkyl or alkoxy radical being unsubstituted or mono-substituted     with a —CN group or mono- or poly-substituted with halogen, with the     proviso that at least one of L¹¹, L¹², L¹³ and L¹⁴ is not hydrogen, -   X¹¹ is halogen, —CN, —NCS, —SF₅, —S—R^(z), —SO_(2—R) ^(z), an alkyl     or alkoxy radical having from 1 to 15 carbon atoms, wherein one or     more methylene groups of said alkyl or alkoxy radical may be     replaced independently of each other by —O—, —S—, —SiR^(x)R^(y)—,     —CH═CH—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen and/or sulfur     atoms are not linked directly to each other, said alkyl or alkoxy     radical being unsubstituted or mono-substituted with a —CN group or     mono- or poly-substituted with halogen; -   R^(x) and R^(y) are each independently of each other hydrogen or an     alkyl radical having from 1 to 7 carbon atoms; -   R^(z) is an alkyl radical having from 1 to 7 carbon atoms, said     alkyl radical being unsubstituted or mono- or poly-substituted with     halogen; A¹¹, A¹², A¹³ and A¹⁴ are each independently of each other     a ring of one of the following formulas: -    whereby each of A¹¹, A¹², A¹³ and A¹⁴ may be the same ring or two     different rings if present twice; -   Y¹¹, Y¹², Y¹³ and Y¹⁴ are each independently of each other hydrogen,     halogen, CN, an alkyl or alkoxy radical having from 1 to 15 carbon     atoms wherein one or more methylene groups of said alkyl or alkoxy     radical may be replaced independently of each other by —O—, —S—,     —SiR^(x)R^(y)—, —CH═CH—, —C≡C—, —CO—O— and/or —O—CO— such that     oxygen and/or sulfur atoms are not linked directly to each other,     said alkyl or alkoxy radical being unsubstituted or mono- or     poly-substituted with halogen, -   f, g and h are each independently of each other 0, 1, 2 or 3; -   Z¹¹, Z¹², Z¹³ and Z¹⁴ are independently of each other a single bond,     —(CH₂)₄)—, —CH₂CH₂—, —CF₂—CF₂—, —CF₂—CH₂—, —CH₂—CF₂—, —CH═CH—,     —CF═CF—, —CF=CH—, —(CH₂)₃O—, —O(CH₂)₃—, —CH=CF—, —C—C—, —CH₂O—,     —OCH₂—, —CF₂O—, —OCF₂—, —CO—O— or —O—CO— whereby each of Z¹¹, Z¹²,     Z¹³ and Z¹⁴ may have the same or a different meaning if present     twice; -   b) 5-80% by weight of a component B containing at least one compound     of the formula II     wherein -   R¹² has the meaning given for R¹¹ -   A¹, A², A³ are each independently of each other -   Z¹ and Z² are independently of each other a single bond, —(CH₂)₄)—,     —CH₂CH₂—, —CF₂—CF₂—, —CF₂—CH₂—, —CH₂—CF₂—, —CH═CH—, —CF═CF—,     —CF═CH—, —(CH₂)₃O—, —O(CH₂)₃—, —CH═CF—, —C≡C—, —CH₂O—, —OCH₂—,     —CF₂O—, —OCF₂—, —CO—O— or —O—CO— whereby each of Z¹¹, Z¹², Z¹³ and     Z¹⁴ may have the same or a different meaning if present twice; -   X¹² is halogen, —CN, —NCS, —SF₅, —SO₂CF₃, alkyl, alkenyl, alkenyloxy     or alkylalkoxy or alkoxy ratical each mono- or polysubstituted by CN     and/or halogen, -   L¹ and L² are each independently of each other H or F, and -   m and n are each independently of each other 0, 1, or 2 and m+n≦2; -   c) 1-20% by weight of component C containing at least one chiral     compound with a HTP of ≦20 μm.

The compounds of the formula I have a broad range of applications. In the pure state, the compounds of the formula I are colourless and are stable chemically, thermally and to light.

Preferably, the compounds according to general formula I do not comprise more than four rings in total, i.e. a+b+c+d≦3. It is even more preferred that a+b+c+d is at least 1 and not more than 3. Most preferred are compounds according to the invention with a+b+c+d being 2 or 3.

It is also preferred that in general formula I a is 1 and b is zero so that there is only one further ring A¹¹ on the left-hand side of the central ring of the compounds according to general formula I.

With regard to the right-hand side of the central ring of the compounds according to general formula I, it is preferred that at least one ring A¹⁴ is present, i.e. d=1. In one preferred embodiment of the Invention d=1 and c=0. In another preferred embodiment of the invention both c and d are equal to 1, and hence there are two rings A¹³ and A¹⁴ present on the right-hand side of the central ring of formula I.

In formula I, R¹¹ is preferably an alkyl or alkoxy radical having from 1 to 10 carbon atoms, wherein one or more methylene groups of said alkyl or alkoxy radical may be replaced independently of each other by —O—, —SiR^(x)R^(y)—, with R^(x) and R^(y) being independently of each other straight-chain alkyl radicals with 1 to 5 carbon atoms, and/or —CH═CH— such that oxygen atoms are not linked directly to each other, said alkyl or alkoxy radical being unsubstituted or mono- or poly-substituted with fluorine. It is even more preferred that R¹¹ is a straight-chain alkyl, alkenyl, alkoxy, alkenyloxy or —O-alkylene-O-alkyl radical or a —O-alkylene-Si(alkyl′)₂-O—Si(alkyl′)₃ radical with up to 10 carbon atoms which radicals may be additionally substituted with fluorine whereby alkyl′ is preferably a straight-chain alkanyl radical with 1, 2, 3 or 4 carbon atoms. It is still more preferred that R¹¹ is one of the following radicals: C_(n)H_(2n+1)—O— with n being 1, 2, 3, 4, 5, 6, 7 or 8; C_(m)H_(2m−1)—O— with m being 2, 3, 4, 5, 6, 7 or 8; C_(p)H_(2p+1)—O—C_(q)H_(2q)—O— with p being 1, 2, 3, 4 or 5 and q being 1, 2, 3, 4 or 5; (C_(t)H_(2t+1))₃Si—O—Si(C_(s)H_(2s+1))₂—C_(r)H_(2r)—O— with r being 1, 2, 3 or 4 and s and t being independently of each other 1, 2, 3 or 4. Especially, R¹¹ is —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—(CH₂)₂—CH═CH₂, —O—(CH₂)₃—CH═CH₂, —O—(CH₂)₄—CH═CH₂, —O—(CH₂)₂—O—CH₃, —O—(CH₂)₂—O—C₂H₅, (CH₃)₃Si—O—Si(CH₃)₂—(CH₂)₂—O—, (CH₃)₃Si—O—Si(CH₃)₂—(CH₂)₃—O—. R¹² is preferably straight chain alkyl with 1 to 6 carbon atoms.

In formula I, L¹¹ is preferably an alkyl or alkoxy radical having from 1 to 10 carbon atoms, wherein one or more methylene groups of said alkyl or alkoxy radical may be replaced independently of each other by —O—, —SiR^(x)R^(y)—, with R^(x) and R^(y) being independently of each other straight-chain alkyl radicals with 1 to 5 carbon atoms, and/or —CH═CH— such that oxygen atoms are not linked directly to each other, said alkyl or alkoxy radical being unsubstituted or mono- or poly-substituted with fluorine. It is even more preferred that L¹¹ is a straight-chain alkyl, alkenyl, alkoxy, alkenyloxy or —O-alkylene-O-alkyl radical or a —O-alkylene-Si(alkyl′)₂—O—Si(alkyl′)₃ radical with up to 10 carbon atoms which radicals may be additionally substituted with fluorine whereby alkyl′ is preferably a straight-chain alkanyl radical with 1, 2, 3 or 4 carbon atoms. It is still more preferred that L¹¹ is one of the following radicals: C_(n)H_(2n+1)—O— with n being 1, 2, 3, 4, 5, 6, 7 or 8 whereby one or more of the H atoms may be replaced by F; C_(m)H_(2m−1)—O— with m being 2, 3, 4, 5, 6, 7 or 8 whereby one or more of the H atoms may be replaced by F; C_(p)H_(2p+1)—O—C_(q)H_(2q)—O— with p being 1, 2, 3, 4 or 5 and q being 1, 2, 3, 4 or 5; (C_(t)H_(2t+1))₃Si—O—Si(C_(s)H_(2s+1))₂—C_(r)H_(2r)—O— with r being 1, 2, 3 or 4 and s and t being independently of each other 1, 2, 3 or 4. Especially, L¹¹ is —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉, —O—(CH₂)₂—CH═CH₂, —O—(CH₂)₃—CH═CH₂, —O—(CH₂)₄—CH═CH₂, —O—(CH₂)₂—O—CH₃, —O—(CH₂)₂—O—C₂H₅, (CH₃)₃Si—O—Si(CH₃)₂-(CH₂)₂—O—, (CH₃)₃Si—O—Si(CH₃)₂—(CH₂)₃—O—.

In formula I, L¹² is preferably fluorine, an alkyl or alkoxy radical having from 1 to 10 carbon atoms, wherein one or more methylene groups of said alkyl or alkoxy radical may be replaced independently of each other by —O—, —SiR^(x)R^(y)—, with R^(x) and R^(y) being independently of each other straight-chain alkyl radicals with 1 to 5 carbon atoms, and/or —CH═CH— such that oxygen atoms are not linked directly to each other, said alkyl or alkoxy radical being unsubstituted or mono- or poly-substituted with fluorine. It is even more preferred that L¹² is F, a straight-chain alkyl, alkenyl, alkoxy, alkenyloxy or —O-alkylene-O-alkyl radical or a —O-alkylene-Si(alkyl′)₂—O—Si(alkyl′)₃ radical with up to 10 carbon atoms which radicals may be additionally substituted with fluorine whereby alkyl′ is preferably a straight-chain alkanyl radical with 1, 2, 3 or 4 carbon atoms. It is still more preferred that L¹² is either F or one of the following radicals: C_(n)H₂₊₁—O— with n being 1, 2, 3, 4, 5, 6, 7 or 8 whereby one or more of the H atoms may be replaced by F; C_(m)H_(2m−1)—O— with m being 2, 3, 4, 5, 6, 7 or 8 whereby one or more of the H atoms may be replaced by F; C_(p)H_(2p+1)—O—C_(q)H_(2q)—O— with p being 1, 2, 3, 4 or 5 and q being 1, 2, 3, 4 or 5; (C_(t)H_(2t+1))₃Si—O—Si(C_(s)H_(2s+1))₂—C_(r)H_(2r)—O— with r being 1, 2, 3 or 4 and s and t being independently of each other 1, 2, 3 or 4. Especially, L¹² is —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉, —O—(CH₂)₂—CH═CH₂, —O —(CH₂)₃—CH═CH₂, —O—(CH₂)₄—CH═CH₂, —O—(CH₂)₂—O—CH₃, —O—(CH₂)₂—O—C₂H₅, (CH₃)₃Si—O—Si(CH₃)₂—(CH₂)₂—O—, (CH₃)₃Si—O—Si(CH₃)₂—(CH₂)₃—O—.

It is also preferred that L¹¹ and L¹² have the same meaning, most preferably L¹¹=L¹²=alkoxy, especially OCH₃, OC₂H₅ or OC₃H₇.

It is preferred that X¹¹ is a polar substituent. Hence, X¹¹ is preferably F, Cl, —NCS, —SF₅, —SO₂R^(z), with R^(z) being a straight-chain alkyl radical that is mono- or poly-substituted with fluorine, —CN, F, Cl, an alkyl or alkoxy radical having from 1 to 10 carbon atoms, wherein one or more methylene groups of said alkyl or alkoxy radical may be replaced independently of each other by —O—, —S—, —SiR^(x)R^(y)—, with R^(x) and R^(y) are independently of each other straight-chain alkyl radicals with 1 to 5 carbon atoms, or —CH═CH— such that oxygen and/or sulfur atoms are not linked directly to each other, said alkyl radical being mono- or poly-substituted with fluorine and said alkoxy radical being unsubstituted or mono- or poly-substituted with fluorine. In one preferred embodiment of the invention, X¹¹ is —NCS, —SF₅ or —SO_(2—R) ^(z), with R^(z) being a straight-chain alkyl radical that is mono- or poly-substituted with fluorine, especially —CF₃, —C₂F₅ or n-C₄F₉. In another preferred embodiment of the invention, X¹¹ is also selected from F, Cl, CN, an alkyl, alkenyl or alkoxy radical having up to 8 carbon atoms said alkyl or alkenyl radical being mono- or poly-substituted with fluorine and said alkoxy radical being unsubstituted or mono- or poly-substituted with fluorine. It is even more preferred that X¹¹ is F, CF₃, CHF₂, C₂F₅, —CH═CF₂, —CF═CF₂, —O—CH₃, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉. A¹¹, A¹², A¹³ and A¹⁴ are preferably independently of each other preferably selected from one of the following formulas:

Preferably, Y¹¹ is F, Cl, CN, an alkoxy, alkenyloxy or —O-alkylene-O-alkyl radical or a —O-alklylene-Si(alkyl′)₂-O—Si(alkyl′)₃ radical with up to 10 carbon atoms which radicals may be additionally substituted with fluorine whereby alkyl′ is preferably a straight-chain alkanyl radical with 1, 2, 3 or 4 carbon atoms. It is still more preferred that y¹¹ is one of the following radicals: C_(n)H_(2n+1)—O— with n being 1, 2, 3, 4, 5, 6, 7 or 8 whereby one or more of the H atoms may be replaced by F; C_(m)H_(2m−1)—O— with m being 2, 3, 4, 5, 6, 7 or 8 whereby one or more of the H atoms may be replaced by F; C_(p)H_(2p+1)—O—C_(q)H_(2q)—O— with p being 1, 2, 3, 4 or 5 and q being 1, 2, 3, 4 or 5; (C_(t)H_(2t+1))₃Si—O—Si(C_(s)H_(2s+1))₂—C_(r)H_(2r)—O— with r being 1, 2, 3 or 4 and s and t being independently of each other 1, 2, 3 or 4. Especially, Y¹¹ is —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉, —O—(CH₂)₂—CH═CH₂, —O—(CH₂)₃—CH═CH₂, —O—(CH₂)₄—CH═CH₂, —O—(CH₂)₂—O—CH₃, —O—(CH₂)₂—O—C₂H₅, (CH₃)₃Si—O—Si(CH₃)₂—(CH₂)₂—O—, (CH₃)₃Si—O—Si(CH₃)₂—(CH₂)₃—O—.

Preferably, Y¹² is F, Cl, CN, hydrogen or has the same meaning as the preferred definitions of Y¹¹ above. Especially, Y¹² is H or F.

Further it is preferred that the compounds according to the invention comprise at least one tetrahydropyran-2,5-diyl, naphthyl-2,6-diyl and/or thien-2,5-diyl ring whereby said naphthyl moiety may be substituted with one or more fluorine atoms. It is even more preferred that one of A¹¹, A¹², A¹³ and A¹⁴ in formula I is

with f and g being independently of each other 0, 1, 2 or 3; especially, f is 1 and g is 2.

In certain preferred embodiments in formula I at least one of A¹¹ and A¹² and especially A¹¹ is a tetrahydropyran-2,5-diyl ring. In other preferred embodiments of the invention at least one of A¹³ and A¹⁴ and particularly only one of A¹³ and A¹⁴ is of the formula

with f and g being independently of each other 0, 1, 2 or 3. It is highly preferred that f is 1 and g is 2 and the fluorine substituents are located in the 1-, 3- and 8-position, respectively, of the naphthyl moiety so that all fluorine subtituents have the same orientation as X¹¹, i.e. to the right hand of the compound according to formula I. In a particularly preferred embodiment one of A¹¹ and A¹² is a tetrahydropyran-2,5-diyl moiety and one of A¹³ and A¹⁴ is an optionally fluorinated naphtha -2,6-diyl moiety.

In another preferred embodiment in formula I A¹⁴-X¹¹ is of the following formula:

wherein X¹¹ is as defined above and preferably NCS, SF₅, —SO₂—CF₃, —SO₂—C₂F₅, —SO₂-n-C₄F₉, —CN, F, Cl, CF₃, CHF₂, C₂F₅, —CH═CF₂, —CF═CF₂, —O—CH₃, —O—C₃H₇, —O-n-C₄H₉, —O—n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉, more preferably F, OCF₃, CF₃, CN, NCS, especially F.

It is furthermore preferred that in formula I Z¹¹, Z¹², Z¹³ and Z¹⁴ are independently of each other a single bond, —CF₂—CF₂—, —CF₂—CH₂—, —CH₂—CF₂—, —CF═CF—, —CF═CH—, —CH═CF—, —C≡C—, —CF₂O— or —CO—O—. It is even more preferred that Z¹¹ and Z¹² are independently of each other a single bond or —CO—O—, especially a single bond, and that Z¹³ and Z¹⁴ are independently of each other a single bond, —CF₂O— or —CO—O—; especially one of Z¹³ and Z¹⁴ is —CF₂O—.

One preferred embodiment of the invention comprises mixtures containing compounds of the formula IA:

wherein

-   c is 0 or 1; -   R¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy or —O-alkylene-O-alkyl radical having     from 2 to 15 carbon atoms, wherein one or more methylene groups of     each of said radicals may be replaced independently of each other by     —S—, —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen     and/or sulfur atoms are not linked directly to each other, said     radicals being unsubstituted or mono-substituted with a —CN group or     mono- or poly-substituted with halogen; preferably R¹¹ is a     straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or     —O-alkylene-O-alkyl radical with up to 10 carbon atoms, said     radicals being unsubstituted or mono- or poly-substituted with     halogen; -   L¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy or —O-alkylene-O-alkyl radical having     from 2 to 15 carbon atoms, wherein one or more methylene groups of     each of said radicals may be replaced independently of each other by     —S—, —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen     and/or sulfur atoms are not linked directly to each other, said     radicals being unsubstituted or mono-substituted with a —CN group or     mono- or poly-substituted with halogen; preferably L¹¹ is a     straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or     —O-alkylene-O-alkyl radical with up to 10 carbon atoms, said     radicals being unsubstituted or mono- or poly-substituted with     halogen; -   L¹² is hydrogen, halogen, an alkyl or alkoxy radical having from 1     to 15 carbon atoms or an alkenyl or alkenyloxy or     —O-alkylene-O-alkyl radical having from 2 to 15 carbon atoms,     wherein one or more methylene groups of each of said radicals may be     replaced independently of each other by —S—, —SiR^(x)R^(y)—, —C≡C—,     —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not     linked directly to each other, said radicals being unsubstituted or     mono-substituted with a —CN group or mono- or poly-substituted with     halogen; preferably L¹² is H, F, a straight-chain alkyl, alkoxy,     alkenyl, alkenyloxy or —O-alkylene-O-alkyl radical with up to 10     carbon atoms, said radicals being unsubstituted or mono- or     poly-substituted with halogen; -   L¹⁵, L¹⁶, L¹⁷ and L¹⁸ are independently of each other H or F;     preferably at least L¹⁵ is F; -   Z¹⁴ is a single bond, —CH₂CH₂—, (—CH₂CH₂—)₂, —CF₂—CF₂—, —CF₂—CH₂—,     —CH₂—CF₂—, —CH═CH—, —CF═CF—, —CF═CH—, —CH═CF—, —C≡C—, —CH₂O—,     —OCH₂—, —CF₂O—, —OCF₂—, —CO—O— or —O—CO—; preferably Z¹⁴ is a single     bond, —C≡C—, —CF₂O— or —CO₂—, in particular a single bond or —CF₂O—; -   X¹¹ is F, Cl, CF₃, OCF₃, CN, NCS, —SF₅ or —SO₂—R^(z); -   R^(x) and R^(y) are independently of each other hydrogen or an alkyl     radical having from 1 to 7 carbon atoms; preferably R^(x) and R^(y)     are both methyl, ethyl, propyl or butyl; and -   R^(z) is an alkyl radical having from 1 to 7 carbon atoms, said     alkyl radical being unsubstituted or mono- or poly-substituted with     halogen; preferably R^(z) is CF₃, C₂F₅ or n-C₄F₉.

One preferred subgroup of compounds according to formula IA are compounds in which c is zero. Examples of compounds of said subgroup are the following ones:

wherein n and m are independently of each other integers from 1 to 8, preferably 1, 2, 3, 4, 5 or 6; p is an integer from 1 to 5, preferably 1, 2 or 4; q and r are independently of each other integers from 2 to 8, preferably 3, 4, 5, 6; s and t are independently of each other 1, 2, 3, 4, preferably 2 or 3; and u and v are independently of each other 1, 2, 3, 4, preferably 1 or 4. Preferably, C_(n)H_(2n+1)O and C_(m)H_(2m+1)O represent independently of each other methoxy, ethoxy, propoxy, n-butoxy, n-pentoxy and n-hexoxy. If present twice in the same compound, both C_(m)H_(2m+1)O substituents may have the same value for m or different ones; preferably m in two C_(m)H_(2m+1)O substituents have the same meaning. Preferably, —SO₂—C_(p)H_(2p+1) represents —SO₂—CF₃, —SO₂—C₂F₅, —SO₂—C₄F₉. Preferably, C_(q)H_(2q-1)O and C_(r)H_(2r-1)O represent —O—CH₂CH═CH₂, —O—(CH₂)₂CH═CH₂, —O—(CH₂)₃CH═CH₂, —O—(CH₂)₂CH═CH—CH₃. Preferably, —OC_(s)H_(2s)OC_(t)H_(2t+1) represents CH₃OCH₂CH₂O— and CH₃CH₂OCH₂CH₂O—. Preferably, (C_(v)H_(2v+1))₃SiOSi(C_(u)H_(2u+1))₂C_(s)H_(2s)O represents (CH₃)₃SiOSi(CH₃)₂CH₂CH₂O— and (CH₃)₃SiOSi(CH₃)₂CH₂CH₂CH₂O—.

Another preferred subgroup of compounds according to formula IA are compounds in which c is 1. Examples of compounds of said subgroup are the following ones:

wherein L^(a) and L^(b) are independently of each other H or F; n and m are independently of each other integers from 1 to 8, preferably 1, 2, 3, 4, 5 or 6; p is an integer from 1 to 5, preferably 1, 2 or 4; q and r are independently of each other Integers from 2 to 8, preferably 3, 4, 5, 6; s and t are independently of each other 1, 2, 3, 4, preferably 2 or 3; and u and v are independently of each other 1, 2, 3, 4, preferably 1 or 4. Preferably, at least one of L^(a) and L^(b) is F, and especially preferably, both L^(a) and L^(b) are F. If present twice in the same compound, both C_(m)H_(2m+1)O substituents may have the same value for m or different ones; preferably m in two C_(m)H_(2m+1)O substituents have the same meaning. Preferably, C_(n)H_(2n+1)O and C_(m)H_(2m+1)O represent independently of each other methoxy, ethoxy, propoxy, n-butoxy, n-pentoxy and n-hexoxy. Preferably, —SO₂—C_(p)H_(2p+l) represents —SO₂—CF₃, —SO₂—C₂F₅, —SO₂—C₄F₉. Preferably, C_(q)H_(2q-1)O and C_(r)H_(2r-1)O represent —O—CH₂CH═CH₂, —O—(CH₂)₂CH═CH₂, —O—(CH₂)₃CH═CH₂, —O—(CH₂)₂CH═CH—CH₃. Preferably, —OC_(s)H_(2s)OC_(t)H_(2t+1) represents CH₃OCH₂CH₂O— and CH₃CH₂OCH₂CH₂O—. Preferably, (C_(v)H_(2v+1))₃SiOSi(C_(u)H_(2u+1))₂C_(s)H_(2s)O represents (CH₃)₃SiOSi(CH₃)₂CH₂CH₂O— and (CH₃)₃SiOSi(CH₃)₂CH₂CH₂CH₂O—.

Still another preferred subgroup of compounds according to formula IA are compounds of formula IAc.

Preferred meanings of the moieties L^(a), L^(c), X¹¹ and Z¹⁴ are given in Table 1 below while R^(a)O represents methoxy, ethoxy, propoxy, n-butoxy, n-pentoxy or n-hexoxy. TABLE 1 Compound IAc-No. L^(a) L^(c) X¹¹ Z¹⁴ -1 H H CF₂CF₂ F -2 H H CF₂CF₂ Cl -3 H H CF₂CF₂ CF₃ -4 H H CF₂CF₂ CHF₂ -5 H H CF₂CF₂ OCF₃ -6 H H CF₂CF₂ OCHF₂ -7 H H CF₂CF₂ CN -8 H H CF₂CF₂ SF₅ -9 H H CF₂CF₂ NCS -10 H H CF₂CF₂ SO₂CF₃ -11 H F CF₂CF₂ F -12 H F CF₂CF₂ Cl -13 H F CF₂CF₂ CF₃ -14 H F CF₂CF₂ CHF₂ -15 H F CF₂CF₂ OCF₃ -16 H F CF₂CF₂ OCHF₂ -17 H F CF₂CF₂ CN -18 H F CF₂CF₂ SF₅ -19 H F CF₂CF₂ NCS -20 H F CF₂CF₂ SO₂CF₃ -21 F F CF₂CF₂ F -22 F F CF₂CF₂ Cl -23 F F CF₂CF₂ CF₃ -24 F F CF₂CF₂ CHF₂ -25 F F CF₂CF₂ OCF₃ -26 F F CF₂CF₂ OCHF₂ -27 F F CF₂CF₂ CN -28 F F CF₂CF₂ SF₅ -29 F F CF₂CF₂ NCS -30 F F CF₂CF₂ SO₂CF₃ -31 H H CF₂CH₂ F -32 H H CF₂CH₂ Cl -33 H H CF₂CH₂ CF₃ -34 H H CF₂CH₂ CHF₂ -35 H H CF₂CH₂ OCF₃ -36 H H CF₂CH₂ OCHF₂ -37 H H CF₂CH₂ CN -38 H H CF₂CH₂ SF₅ -39 H H CF₂CH₂ NCS -40 H H CF₂CH₂ SO₂CF₃ -41 H F CF₂CH₂ F -42 H F CF₂CH₂ Cl -43 H F CF₂CH₂ CF₃ -44 H F CF₂CH₂ CHF₂ -45 H F CF₂CH₂ OCF₃ -46 H F CF₂CH₂ OCHF₂ -47 H F CF₂CH₂ CN -48 H F CF₂CH₂ SF₅ -49 H F CF₂CH₂ NCS -50 H F CF₂CH₂ SO₂CF₃ -51 F F CF₂CH₂ F -52 F F CF₂CH₂ Cl -53 F F CF₂CH₂ CF₃ -54 F F CF₂CH₂ CHF₂ -55 F F CF₂CH₂ OCF₃ -56 F F CF₂CH₂ OCHF₂ -57 F F CF₂CH₂ CN -58 F F CF₂CH₂ SF₅ -59 F F CF₂CH₂ NCS -60 F F CF₂CH₂ SO₂CF₃ -61 H H CH₂CF₂ F -62 H H CH₂CF₂ Cl -63 H H CH₂CF₂ CF₃ -64 H H CH₂CF₂ CHF₂ -65 H H CH₂CF₂ OCF₃ -66 H H CH₂CF₂ OCHF₂ -67 H H CH₂CF₂ CN -68 H H CH₂CF₂ SF₅ -69 H H CH₂CF₂ NCS -70 H H CH₂CF₂ SO₂CF₃ -71 H F CH₂CF₂ F -72 H F CH₂CF₂ Cl -73 H F CH₂CF₂ CF₃ -74 H F CH₂CF₂ CHF₂ -75 H F CH₂CF₂ OCF₃ -76 H F CH₂CF₂ OCHF₂ -77 H F CH₂CF₂ CN -78 H F CH₂CF₂ SF₅ -79 H F CH₂CF₂ NCS -80 H F CH₂CF₂ SO₂CF₃ -81 F F CH₂CF₂ F -82 F F CH₂CF₂ Cl -83 F F CH₂CF₂ CF₃ -84 F F CH₂CF₂ CHF₂ -85 F F CH₂CF₂ OCF₃ -86 F F CH₂CF₂ OCHF₂ -87 F F CH₂CF₂ CN -88 F F CH₂CF₂ SF₅ -89 F F CH₂CF₂ NCS -90 F F CH₂CF₂ SO₂CF₃ -91 H H —CF═CF— F -92 H H —CF═CF— Cl -93 H H —CF═CF— CF₃ -94 H H —CF═CF— CHF₂ -95 H H —CF═CF— OCF₃ -96 H H —CF═CF— OCHF₂ -97 H H —CF═CF— CN -98 H H —CF═CF— SF₅ -99 H H —CF═CF— NCS -100 H H —CF═CF— SO₂CF₃ -101 H F —CF═CF— F -102 H F —CF═CF— Cl -103 H F —CF═CF— CF₃ -104 H F —CF═CF— CHF₂ -105 H F —CF═CF— OCF₃ -106 H F —CF═CF— OCHF₂ -107 H F —CF═CF— CN -108 H F —CF═CF— SF₅ -109 H F —CF═CF— NCS -110 H F —CF═CF— SO₂CF₃ -111 F F —CF═CF— F -112 F F —CF═CF— Cl -113 F F —CF═CF— CF₃ -114 F F —CF═CF— CHF₂ -115 F F —CF═CF— OCF₃ -116 F F —CF═CF— OCHF₂ -117 F F —CF═CF— CN -118 F F —CF═CF— SF₅ -119 F F —CF═CF— NCS -120 F F —CF═CF— SO₂CF₃ —CF₂O— -121 H H CF₂CF₂ F -122 H H CF₂CF₂ Cl -123 H H CF₂CF₂ CF₃ -124 H H CF₂CF₂ CHF₂ -125 H H CF₂CF₂ OCF₃ -126 H H CF₂CF₂ OCHF₂ -127 H H CF₂CF₂ CN -128 H H CF₂CF₂ SF₅ -129 H H CF₂CF₂ NCS -130 H H CF₂CF₂ SO₂CF₃ -131 H F CF₂CF₂ F -132 H F CF₂CF₂ Cl -133 H F CF₂CF₂ CF₃ -134 H F CF₂CF₂ CHF₂ -135 H F CF₂CF₂ OCF₃ -136 H F CF₂CF₂ OCHF₂ -137 H F CF₂CF₂ CN -138 H F CF₂CF₂ SF₅ -139 H F CF₂CF₂ NCS -140 H F CF₂CF₂ SO₂CF₃ -141 F F CF₂CF₂ F -142 F F CF₂CF₂ Cl -143 F F CF₂CF₂ CF₃ -144 F F CF₂CF₂ CHF₂ -145 F F CF₂CF₂ OCF₃ -146 F F CF₂CF₂ OCHF₂ -147 F F CF₂CF₂ CN -148 F F CF₂CF₂ SF₅ -149 F F CF₂CF₂ NCS -150 F F CF₂CF₂ SO₂CF₃ single -151 H H CF₂CF₂ F -152 H H CF₂CF₂ Cl -153 H H CF₂CF₂ CF₃ -154 H H CF₂CF₂ CHF₂ -155 H H CF₂CF₂ OCF₃ -156 H H CF₂CF₂ OCHF₂ -157 H H CF₂CF₂ CN -158 H H CF₂CF₂ SF₅ -159 H H CF₂CF₂ NCS -160 H H CF₂CF₂ SO₂CF₃ -161 H F CF₂CF₂ F -162 H F CF₂CF₂ Cl -163 H F CF₂CF₂ CF₃ -164 H F CF₂CF₂ CHF₂ -165 H F CF₂CF₂ OCF₃ -166 H F CF₂CF₂ OCHF₂ -167 H F CF₂CF₂ CN -168 H F CF₂CF₂ SF₅ -169 H F CF₂CF₂ NCS -170 H F CF₂CF₂ SO₂CF₃ -171 F F CF₂CF₂ F -172 F F CF₂CF₂ Cl -173 F F CF₂CF₂ CF₃ -174 F F CF₂CF₂ CHF₂ -175 F F CF₂CF₂ OCF₃ -176 F F CF₂CF₂ OCHF₂ -177 F F CF₂CF₂ CN -178 F F CF₂CF₂ SF₅ -179 F F CF₂CF₂ NCS -180 F F CF₂CF₂ SO₂CF₃ —COO— -181 H H CF₂CF₂ F -182 H H CF₂CF₂ Cl -183 H H CF₂CF₂ CF₃ -184 H H CF₂CF₂ CHF₂ -185 H H CF₂CF₂ OCF₃ -186 H H CF₂CF₂ OCHF₂ -187 H H CF₂CF₂ CN -188 H H CF₂CF₂ SF₅ -189 H H CF₂CF₂ NCS -190 H H CF₂CF₂ SO₂CF₃ -191 H F CF₂CF₂ F -192 H F CF₂CF₂ Cl -193 H F CF₂CF₂ CF₃ -194 H F CF₂CF₂ CHF₂ -195 H F CF₂CF₂ OCF₃ -196 H F CF₂CF₂ OCHF₂ -197 H F CF₂CF₂ CN -198 H F CF₂CF₂ SF₅ -199 H F CF₂CF₂ NCS -200 H F CF₂CF₂ SO₂CF₃ -201 F F CF₂CF₂ F -202 F F CF₂CF₂ Cl -203 F F CF₂CF₂ CF₃ -204 F F CF₂CF₂ CHF₂ -205 F F CF₂CF₂ OCF₃ -206 F F CF₂CF₂ OCHF₂ -207 F F CF₂CF₂ CN -208 F F CF₂CF₂ SF₅ -209 F F CF₂CF₂ NCS -210 F F CF₂CF₂ SO₂CF₃

Still another preferred embodiment of the invention comprises compounds of formula IB:

wherein

-   R¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy radical having from 2 to 15 carbon atoms     or an —O-alkylene-O-alkyl radical having from 2 to 15 carbon atoms,     wherein one or more methylene groups of each of said radicals may be     replaced independently of each other by —S—, —SiR^(x)R^(y)—, —C≡C—,     —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not     linked directly to each other, said radicals being unsubstituted or     mono-substituted with a —CN group or mono- or poly-substituted with     halogen; preferably R¹¹ is a straight-chain alkyl, alkoxy, alkenyl,     alkenyloxy or —O-alkylene-O-alkyl radical with up to 10 carbon     atoms, said radicals being unsubstituted or mono- or     poly-substituted with halogen; -   L¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy radical having from 2 to 15 carbon atoms     or an —O-alkylene-O-alkyl radical having from 2 to 15 carbon atoms,     wherein one or more methylene groups of each of said radicals may be     replaced independently of each other by —S—, —SiR^(x)R^(y)—, —C≡C—,     —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not     linked directly to each other, said radicals being unsubstituted or     mono-substituted with a —CN group or mono- or poly-substituted with     halogen; preferably L¹¹ is a straight-chain alkyl, alkoxy, alkenyl,     alkenyloxy or —O-alkylene-O-alkyl radical with up to 10 carbon     atoms, said radicals being unsubstituted or mono- or     poly-substituted with halogen; -   L¹² is hydrogen, halogen, an alkyl or alkoxy radical having from 1     to 15 carbon atoms or an alkenyl or alkenyloxy radical having from 2     to 15 carbon atoms or an —O-alkylene-O-alkyl radical having from 2     to 15 carbon atoms, wherein one or more methylene groups of each of     said radicals may be replaced independently of each other by —S—,     —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen and/or     sulfur atoms are not linked directly to each other, said radicals     being unsubstituted or mono-substituted with a —CN group or mono- or     poly-substituted with halogen; preferably L¹² is H, F, a     straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or     —O-alkylene-O-alkyl radical with up to 10 carbon atoms, said     radicals being unsubstituted or mono- or poly-substituted with     halogen;     whereby it is further preferred that at least one of R¹¹, L¹¹ and     L¹² is one of said straight-chain alkyl, alkoxy, alkenyl, alkenyloxy     or —O-alkylene-O-alkyl radicals; -   L¹⁵ and L¹⁶ are independently of each other H or F; preferably at     least L¹⁵ is F; -   Z¹⁴ is a single bond, —CH₂CH₂—,(—CH₂CH₂—)₂, —CF₂—CF₂—, —CF₂—CH₂—,     —CH₂—CF₂—, —CH═CH—, —CF═CF—, —CF═CH—, —CH═CF—, —C≡C—, —CH₂O—,     —OCH₂—, —CF₂O—, —OCF₂—, —CO—O— or —O—CO—; preferably Z¹⁴ is a single     bond, —CF₂O— or —CO₂—; -   X¹¹ is F, Cl, —CN, —NCS, —SF₅, —SO₂—R^(z), an alkyl or alkoxy     radical having from 1 to 15 carbon atoms, wherein one or more     methylene groups of said alkyl or alkoxy radical may be replaced     independently of each other by —O—, —S—, —SiR^(x)R^(y)—, —CH═CH—,     —C≡C—, —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are     not linked directly to each other, said alkyl or alkoxy radical     being unsubstituted or mono-substituted with a —CN group or mono- or     poly-substituted with halogen; preferably X¹¹ is F, Cl, CF₃, OCF₃,     OCHF₂, NCS, SF₅ or —SO₂—R^(z); -   R^(x) and R^(y) are independently of each other hydrogen or an alkyl     radical having from 1 to 7 carbon atoms; preferably both R^(x) and     R^(y) are methyl, ethyl, propyl or butyl; -   R^(z) is an alkyl radical having from 1 to 7 carbon atoms, said     alkyl radical being unsubstituted or mono- or poly-substituted with     halogen; preferably R^(z) is CF₃, C₂F₅ or n-C₄F₉.

Examples of compounds of said preferred embodiment are the following compounds:

wherein n and m are independently of each other 1, 2, 3, 4, 5, 6, 7 or 8 and X¹¹ is CN, NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉, F, CF₃, CHF₂, C₂F₅, —CH═CF₂, —CF═CF₂, —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, —O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉ with CN, SO₂CF₃, F, CF₃, —O—CF₃ being preferred. Preferably, n and m are the same number and equal to 1, 2, 3, 4, 5 or 6. If present twice in the same compound, both C_(m)H_(2m+1)O substituents may have the same value for m or different ones; preferably m in two C_(m)H_(2m+1)O substituents have the same meaning. Furthermore, one or more of the hydrogen atoms of the C_(n)H_(2n+1), the OC_(n)H_(2n+1) and the OC_(m)H_(2m+1) moiety, respectively, may be replaced by a halogen atom, preferably a fluorine atom. Particularly preferred are compounds of formulas IB-1 to IB-12 with X¹¹ being F, CF₃ or OCF₃, especially F.

Further preferred embodiments of the invention comprise compounds of formulas IC or ID:

wherein

-   R¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy or —O-alkylene-O-alkyl radical having     from 2 to 15 carbon atoms, wherein one or more methylene groups of     each of said radicals may be replaced independently of each other by     —S—, —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen     and/or sulfur atoms are not linked directly to each other, said     radicals being unsubstituted or mono-substituted with a —CN group or     mono- or poly-substituted with halogen; preferably R¹¹ is a     straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or     —O-alkylene-O-alkyl radical with up to 10 carbon atoms, said     radicals being unsubstituted or mono- or poly-substituted with     halogen; -   L¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy or —O-alkylene-O-alkyl radical having     from 2 to 15 carbon atoms, wherein one or more methylene groups of     each of said radicals may be replaced independently of each other by     —S—, —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that     oxygen-and/or sulfur atoms are not linked directly to each other,     said radicals being unsubstituted or mono-substituted with a —CN     group or mono- or poly-substituted with halogen; preferably, L¹¹ is     a straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or     —O-alkylene-O-alkyl radical with up to 10 carbon atoms, said     radicals being unsubstituted or mono- or poly-substituted with     halogen; -   L¹² is hydrogen, halogen, an alkyl or alkoxy radical having from 1     to 15 carbon atoms or an alkenyl or alkenyloxy or     —O-alkylene-O-alkyl radical having from 2 to 15 carbon atoms,     wherein one or more methylene groups of each of said radicals may be     replaced independently of each other by —S—, —SiR^(x)R^(y)—, —C≡C—,     —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not     linked directly to each other, said radicals being unsubstituted or     mono-substituted with a —CN group or mono- or poly-substituted with     halogen;

preferably, L¹² is H, F, a straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or —O-alkylene-O-alkyl radical with up to 10 carbon atoms, said radicals being unsubstituted or mono- or poly-substituted with halogen;

whereby it is preferred that at least one of R¹¹, L¹¹ and L¹² is one of said preferred straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or —O-alkylene-O-alkyl radicals;

-   L¹⁵, L¹⁶, L¹⁷, L¹⁸ and L¹⁹ are independently of each other H or F;     preferably at least L¹⁵ and L¹⁸ are both F; -   Z¹³ and Z¹⁴ are independently of each other a single bond, —CH₂CH₂—,     (—CH₂CH₂—)₂, —CF₂—CF₂—, —CF₂—CH₂—, —CH₂—CF₂—, —CH═CH—, —CF═CF—,     —CF═CH—, —CH═CF—, —C≡C—, —CH₂O—, —OCH₂—, —CF₂O—, —OCF₂—, —CO—O— or     —O—CO— whereby at least one of Z¹³ and Z¹⁴ is a single bond;     preferably Z¹³ and Z¹⁴ are both a single bond or one of Z¹³ and Z¹⁴     is —CF₂O— or —CO₂—; -   X¹¹ is F, Cl, —CN, —NCS, —SF₅, —SO₂—R^(z), an alkyl or alkoxy     radical having from 1 to 15 carbon atoms, wherein one or more     methylene groups of said alkyl or alkoxy radical may be replaced     independently of each other by —O—, —S—, —SiR^(x)R^(y)—, —CH═CH—,     —C≡C—, —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are     not linked directly to each other, said alkyl or alkoxy radical     being unsubstituted or mono-substituted with a —CN group or mono- or     poly-substituted with halogen; preferably X¹¹ is F, Cl, CF₃, OCF₃,     OCHF₂, NCS, SF₅ or —SO₂—R^(z); -   R^(x) and R^(y) are independently of each other hydrogen or an alkyl     radical having from 1 to 7 carbon atoms; preferably both R^(x) and     R^(y) are methyl, ethyl, propyl or butyl; and -   R^(z) is an alkyl radical having from 1 to 7 carbon atoms, said     alkyl radical being unsubstituted or mono- or poly-substituted with     halogen; preferably R^(z) is CF₃, C₂F₅ or n-C₄F₉.

Examples of said preferred compounds of formula IC are the following ones:

wherein n and m are independently of each other 1, 2, 3, 4, 5, 6, 7 or 8; q is 2, 3, 4, 5, 6, 7 or 8; and X¹¹ is CN, NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉, F, CF₃, CHF₂, C₂F₅, —CH═CF₂, —CF═CF₂, —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉ with CN, SO₂CF₃, F, CF₃, —O—CF₃ being preferred. If present twice in the same compound, both C_(m)H_(2m+1)O substituents may have the same value for m or different ones; preferably in two C_(m)H_(2m+1)O substituents m is the same integer. Similarly, if present twice in the same compound, both C_(q)H_(2q-1)O substituents may have the same value for q or different ones; preferably in two C_(q)H_(2q-1)O substituents q is the same integer. Preferably, n and m are the same number and equal to 1, 2, 3, 4, 5 or 6. Furthermore, one or more of the hydrogen atoms of the C_(n)H_(2n+1), the OC_(n)H_(2n+1), the OC_(m)H_(2m+1) and the OC_(q)H_(2q-1) moiety, respectively, may be replaced by a halogen atom, preferably a fluorine atom. Particularly preferred are compounds of formulas IC-1 to IC-25 with X¹¹ being F, CF₃ or OCF₃, especially F.

Examples of said preferred compounds of formula ID are the following ones:

wherein n and m are independently of each other 1, 2, 3, 4, 5, 6, 7 or 8; q is 2, 3, 4, 5, 6, 7 or 8; and X¹¹ is CN, NCS, SF₅, SO₂CF₃; SO₂C₂F₅, SO₂C₄F₉, F, CF₃, CHF₂, C₂F₅, —CH═CF₂, —CF═CF₂, —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉ with CN, SO₂CF₃, F, CF₃, —O—CF₃ being preferred. If present twice in the same compound, both C_(m)H_(2m+1)O substituents may have the same value for m or different ones; preferably in two C_(m)H_(2m+1)O substituents m is the same integer. Similarly, if present twice in the same compound, both C_(q)H_(2q-1)O substituents may have the same value for q or different ones; preferably in two C_(q)H_(2q-1)O substituents q is the same integer. Preferably, n and m are the same number and equal to 1, 2, 3, 4, 5 or 6. Furthermore, one or more of the hydrogen atoms of the C_(n)H_(2n+1), the OC_(n)H_(2n+1), the OC_(m)H_(2m+1) an the C_(q)H_(2q-1) moiety, respectively, may be replaced by a halogen atom, preferably a fluorine atom. Particularly preferred are compounds of formulas ID-1 to ID-60 with X¹¹ being F, CF₃ or OCF₃, especially F.

Further preferred embodiments of the invention comprise compounds of formulas IE or IF:

wherein

-   R¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy or —O-alkylene-O-alkyl radical having     from 2 to 15 carbon atoms, wherein one or more methylene groups of     each of said radicals may be replaced independently of each other by     —S—, —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen     and/or sulfur atoms are not linked directly to each other, said     radicals being unsubstituted or mono-substituted with a —CN group or     mono- or poly-substituted with halogen; preferably R¹¹ is a     straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or     —O-alkylene-O-alkyl radical with up to 10 carbon atoms, said     radicals being unsubstituted or mono- or poly-substituted with     halogen; -   L¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy or —O-alkylene-O-alkyl radical having     from 2 to 15 carbon atoms, wherein one or more methylene groups of     each of said radicals may be replaced independently of each other by     —S—, —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen     and/or sulfur atoms are not linked directly to each other, said     radicals being unsubstituted or mono-substituted with a —CN group or     mono- or poly-substituted with halogen; preferably L¹¹ is a     straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or     —O-alkylene-O-alkyl radical with up to 10 carbon atoms, said     radicals being unsubstituted or mono- or poly-substituted with     halogen; -   L¹² is hydrogen, halogen, an alkyl or alkoxy radical having from 1     to 15 carbon atoms or an alkenyl or alkenyloxy or     —O-alkylene-O-alkyl radical having from 2 to 15 carbon atoms,     wherein one or more methylene groups of each of said radicals may be     replaced independently of each other by —S—, —SiR^(x)R^(y)—, —C≡C—,     —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not     linked directly to each other, said radicals being unsubstituted or     mono-substituted with a —CN group or mono- or poly-substituted with     halogen; preferably L¹² is H, F, a straight-chain alkyl, alkoxy,     alkenyl, alkenyloxy or —O-alkylene-O-alkyl radical with up to 10     carbon atoms, said radicals being unsubstituted or mono- or     poly-substituted with halogen;     whereby at least one of R¹¹, L¹¹ and L¹² is one of said     straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or     —O-alkylene-O-alkyl radicals; -   L¹⁵, L¹⁶, L¹⁷, L¹⁸, L^(19a), L^(19b) and L^(19c) are independently     of each other H or F; preferably both L¹⁷ and L^(19b) are F; -   Z¹⁴ is a single bond, —CH₂CH₂—, (—CH₂CH₂—)₂, —CF₂—CF₂—, —CF₂—CH₂—,     —CH₂—CF₂—, —CH═CH—, —CF═CF—, —CF═CH—, —CH═CF—, —C≡C—, —CH₂O—,     —OCH₂—, —CF₂O—, —OCF₂—, —CO—O— or —O—CO—; preferably Z¹⁴ is a single     bond, —CF₂O— or —CO₂—; -   X¹¹ is F, Cl, —CN, —NCS, —SF₅, —SO_(2—R) ^(z), an alkyl or alkoxy     radical having from 1 to 15 carbon atoms, wherein one or more     methylene groups of said alkyl or alkoxy radical may be replaced     independently of each other by —O—, —S—, —SiR^(x)R^(y)—, —CH═CH—,     —C≡C—, —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are     not linked directly to each other, said alkyl or alkoxy radical     being unsubstituted or mono-substituted with a —CN group or mono- or     poly-substituted with halogen; preferably X¹ is F, Cl, CF₃, OCF₃,     OCHF₂, NCS, SF₅ or —SO₂—R^(z); -   R^(x) and R^(y) are independently of each other hydrogen or an alkyl     radical having from 1 to 7 carbon atoms; preferably both R^(x) and     R^(y) are methyl, ethyl, propyl or butyl; and; -   R^(z) is an alkyl radical having from 1 to 7 carbon atoms, said     alkyl radical being unsubstituted or mono- or poly-substituted with     halogen; preferably R^(z) is CF₃, C₂F₅ or n-C₄F₉.

Examples of said preferred compounds of formula IE are the following ones:

wherein n and m are independently of each other 1, 2, 3, 4, 5, 6, 7 or 8; q and p are independently of each other 2, 3, 4, 5, 6, 7 or 8; and X¹¹ is CN, NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉, F, CF₃, CHF₂, C₂F₅, —CH═CF₂, —CF═CF₂, —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉ with NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉, F, CF₃, OCF₃ being preferred. If present twice in the same compound, both C_(m)H_(2m+1)O substituents may have the same value for m or different ones; preferably in two C_(m)H_(2m+1)O substituents m is the same integer. Similarly, if present twice in the same compound, both. C_(q)H_(2q-1)O substituents may have the same value for q or different ones; preferably in two C_(q)H_(2q-1)O substituents q is the same integer. Preferably, n and m are the same number and equal to 1, 2, 3, 4, 5 or 6. Likewise it is preferred that both q and p are the same number and equal to 3, 4, 5, 6. Furthermore, one or more of the hydrogen atoms of the C_(n)H_(2n+1), the OC_(n)H_(2n+1), the OC_(m)H_(2m+1), the OC_(p)H_(2p-1) and the OC_(q)H_(2q-1) moiety, respectively, may be replaced by a halogen atom, preferably a fluorine atom. Particularly preferred are compounds of formulas IE-1 to IE-36 with X¹¹ being NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉.

Examples of said preferred compounds of formula IF are the following ones:

wherein n and m are independently of each other 1, 2, 3, 4, 5, 6, 7 or 8; q and p are independently of each other 2, 3, 4, 5, 6, 7 or 8; and X¹¹ is CN, NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉, F, CF₃, CHF₂, C₂F₅, —CH═CF₂, —CF—CF₂, —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉ with NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉, F, CF₃, OCF₃ being preferred. If present twice in the same compound, both C_(m)H_(2m+1)O substituents may have the same value for m or different ones; preferably in two C_(m)H_(2m+1)O substituents m is the same integer. Similarly, if present twice in the same compound, both C_(q)H_(2q-1)O substituents may have the same value for q or different ones; preferably in two C_(q)H_(2q-1)O substituents q is the same integer. Preferably, n and m are the same number and equal to 1, 2, 3, 4, 5 or 6. Likewise it is preferred that both q and p are the same number and equal to 3, 4, 5, 6. Furthermore, one or more of the hydrogen atoms of the C_(n)H_(2n+1), the OC_(n)H_(2n+1), the OC_(m)H_(2m+1), the OC_(p)H_(2p-1) and the OC_(q)H_(2q-1) moiety, respectively, may be replaced by a halogen atom, preferably a fluorine atom. Particularly preferred are compounds of formulas IF-1 to IF-72 with X¹¹ being NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉, F, CF₃, OCF₃, especially F.

A further preferred embodiment of the invention comprises compounds of formula IG:

wherein

-   R¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy or —O-alkylene-O-alkyl radical having     from 2 to 15 carbon atoms, wherein one or more methylene groups of     each of said radicals may be replaced independently of each other by     —S—, —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen     and/or sulfur atoms are not linked directly to each other, said     radicals being unsubstituted or mono-substituted with a —CN group or     mono- or poly-substituted with halogen; preferably R¹¹ is a     straight-chain alkyl, alkoxy, alkenyl, alkenyloxy or     —O-alkylene-O-alkyl radical with up to 10 carbon atoms, said     radicals being unsubstituted or mono- or poly-substituted with     halogen; -   L¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy or —O-alkylene-O-alkyl radical having     from 2 to 15 carbon atoms, wherein one or more methylene groups of     each of said radicals may be replaced independently of each other by     —S—, —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen     and/or sulfur atoms are not linked directly to each other, said     radicals being unsubstituted or mono-substituted with a —CN group or     mono- or poly-substituted with halogen; preferably L¹¹ is an alkoxy,     alkenyloxy or —O-alkylene-O-alkyl radical with up to 10 carbon     atoms, said radicals being unsubstituted or mono- or     poly-substituted with halogen; -   L¹² is hydrogen, halogen, an alkyl or alkoxy radical having from 1     to 15 carbon atoms or an alkenyl or alkenyloxy or     —O-alkylene-O-alkyl radical having from 2 to 15 carbon atoms,     wherein one or more methylene groups of each of said radicals may be     replaced. independently of each other by —S—, —SiR^(x)R^(y)—, —C≡C—,     —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not     linked directly to each other, said radicals being unsubstituted or     mono-substituted with a —CN group or mono- or poly-substituted with     halogen; preferably L¹² is H; -   Y¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms     or an alkenyl or alkenyloxy or —O-alkylene-O-alkyl radical having     from 2 to 15 carbon atoms, wherein one or more methylene groups of     each of said radicals may be replaced independently of each other by     —S—, —SiR^(x)R^(y)—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen     and/or sulfur atoms are not linked directly to each other, said     radicals being unsubstituted or mono-substituted with a —CN group or     mono- or poly-substituted with halogen; preferably Yli is an alkoxy,     alkenyloxy or —O-alkylene-O-alkyl radical with up to 10 carbon     atoms, said radicals being unsubstituted or mono- or     poly-substituted with halogen; in particular Y¹¹ has the same     meaning as L¹¹; -   Y¹² is hydrogen, halogen, an alkyl or alkoxy radical having from 1     to 15 carbon atoms or an alkenyl or alkenyloxy or     —O-alkylene-O-alkyl radical having from 2 to 15 carbon atoms,     wherein one or more methylene groups of each of said radicals may be     replaced independently of each other by —S—, —SiR^(x)R^(y)—, —C≡C—,     —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not     linked directly to each other, said radicals being unsubstituted or     mono-substituted with a —CN group or mono- or poly-substituted with     halogen; preferably L¹² is H; -   d is 0, 1 or 2; preferably d is 0 or 1, especially 1; -   L¹⁵ and L¹⁶ are independently of each other H or F; preferably both     L¹⁵ and L¹⁶ are F; -   Z¹⁴ is a single bond, —CH₂CH₂—,(—CH₂CH₂—)₂, —CF₂—CF₂—, —CF₂—CH₂—,     —CH₂—CF₂—, —CH═CH—, —CF═CF—, —CF═CH—, —CH═CF—, —C≡C—, —CH₂O—,     —OCH₂—, —CF₂O—, —OCF₂—, —CO—O— or —O—CO—; preferably Z¹⁴ is a single     bond, —CF₂O— or —CO₂—; -   X¹¹ is F, Cl, —CN, —NCS, —SF₅, —SO₂—R^(z), an alkyl or alkoxy     radical having from 1 to 15 carbon atoms, wherein one or more     methylene groups of said alkyl or alkoxy radical may be replaced     independently of each other by —O—, —S—, —SiR^(x)R^(y)—, —CH═CH—,     —C≡C—, —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are     not linked directly to each other, said alkyl or alkoxy radical     being unsubstituted or mono-substituted with a —CN group or mono- or     poly-substituted with halogen; preferably X¹¹ is F, Cl, CF₃, OCF₃,     OCHF₂, NCS, SF₅ or —SO₂—R^(z); -   R^(x) and R^(y) are independently of each other hydrogen or an alkyl     radical having from 1 to 7 carbon atoms; preferably both R^(x) and     R^(y) are methyl, ethyl, propyl or butyl; and; -   R^(z) is an alkyl radical having from 1 to 7 carbon atoms, said     alkyl radical being unsubstituted or mono- or poly-substituted with     halogen; preferably R^(z) is CF₃, C₂F₅ or n-C₄F₉.

One preferred subgroup of compounds according to formula IG are compounds of formula I in which d is zero. Examples of compounds of said subgroup are the following ones:

wherein m, n and w are independently of each other integers from 1 to 8, preferably 1, 2, 3, 4, 5 or 6; q, y and r are independently of each other integers from 2 to 8, preferably 3, 4, 5, 6; s and t are independently of each other 1, 2, 3, 4, preferably 2 or 3; u and v are independently of each other 1, 2, 3, 4, preferably 1 or 4; and X¹¹ is CN, NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉, F, CF₃, CHF₂, C₂F₅, —CH═CF₂, —CF═CF₂, —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O-n-C₄F₉ with CN, SO₂CF₃, F, CF₃, —O—CF₃ being preferred. Preferably, C_(n)H_(2n+1)O, C_(m)H_(2m+1)O and C_(w)H_(2w+1)O represent independently of each other methoxy, ethoxy, propoxy, n-butoxy, n-pentoxy and n-hexoxy. Preferably, C_(q)H_(2q-1)O, C_(y)H_(2y-1)O and C_(r)H_(2r-1)O represent —O—CH₂CH═CH₂, —O—(CH₂)₂CH═CH₂, —O—(CH₂)₃CH═CH₂, —O—(CH₂)₂CH═CH—CH₃. Preferably, —OC_(s)H_(2s)OC_(t)H_(2t+1) represents CH₃OCH₂CH₂O— and CH₃CH₂OCH₂CH₂O—. Preferably, (C_(v)H_(2v+1))₃SiOSi(C_(u)H_(2u+1))₂C_(r)H_(2s)O represents (CH₃)₃SiOSi(CH₃)₂CH₂CH₂O— and (CH₃)₃SiOSi(CH₃)₂CH₂CH₂CH₂O—. Particularly preferred are compounds of formulas IGa-1 to IGa-8 with X¹¹ being F, CF₃ or OCF₃, especially F.

Another preferred subgroup of compounds according to formula IG are compounds in which d is 1. Examples of compounds of said subgroup are the following ones:

wherein m, n and w are independently of each other integers from 1 to 8, preferably 1, 2, 3, 4, 5 or 6; q, y and r are independently of each other integers from 2 to 8, preferably 3, 4, 5, 6; s and t are independently of each other 1, 2, 3, 4, preferably 2 or 3; u and v are independently of each other 1, 2, 3, 4, preferably 1 or 4; and X¹¹ is CN, NCS, SF₅, SO₂CF₃, SO₂C₂F₅, SO₂C₄F₉, F, CF₃, CHF₂, C₂F₅, —CH═CF₂, —CF═CF₂, —O—CH₃, —O—C₂H₅, —O—C₃H₇, —O-n-C₄H₉, —O-n-C₅H₁₁, O-n-C₆H₁₃, —O—CF₃, —O—CHF₂, —O—C₂F₅, —O—C₃F₇, —O—n-C₄F₉ with CN, SO₂CF₃, F, CF₃, —O—CF₃ being preferred. Preferably, C_(n)H_(2n+1)O, C_(m)H_(2m+1)O and C_(w)H_(2w+1)O represent independently of each other methoxy, ethoxy, propoxy, n-butoxy, n-pentoxy and n-hexoxy. Preferably, C_(y)H_(2y-1)O and C_(r)H_(2r-1)O represent —O—CH₂CH═CH₂, —O—(CH₂)₂CH—CH₂, —O—(CH₂)₃CH═CH₂, —O—(CH₂)₂CH═CH—CH₃. Preferably, —OC_(s)H_(2s)OC_(t)H_(2t+1) represents CH₃OCH₂CH₂O— and CH₃CH₂OCH₂CH₂O—. Preferably, (C_(v)H_(2v+1))₃SiOSi(C_(u)H_(2u+1))₂C_(s)H_(2s)O represents (CH₃)₃SiOSi(CH₃)₂CH₂CH₂O— and (CH₃)₃SiOSi(CH₃)₂CH₂CH₂CH₂O—. Particularly preferred are compounds of formulas IGb-1 to IGb-42 with X¹¹ being F, CF₃ or OCF₃, especially F.

The compounds of formula I are partly known from U.S. Pat. No. 6,177,154 or are prepared by methods known per se, as described in the literature (for example in the standard works, such as Houben-Weyl, Methoden der organischen Chemie [Methods of Organic Chemistry], Georg-Thieme-Verlag, Stuttgart), to be precise under reaction conditions which are known and suitable for the said reactions. Use can also be made here of variants which are known per se, but are not mentioned here in greater detail.

The inventive mixtures contain 1-25 wt. %, preferably 2-20 wt. % and most preferably 3-15 wt. % of component A.

Preferred compounds of component B are compounds of the formulae II-1 to II-8:

In the compounds of the formulae II-1 to II-8 X is preferably F, CN, NCS, CF₃, SF₅ or OCF₃.

R¹² is preferably straight chain alkyl or alkoxy with up to six carbon atoms. Especially preferred are compounds of the formulae II-5 and II-8.

The inventive mixtures contain 20-80 wt. % of the pyrane compounds of the formulae II, preferably 25-70 wt. % and especially preferred 30-60 wt. %.

Suitable chiral compounds of component C are those which have a helical twisting power of >20 μm, preferably >40 μm, most preferably >60 μm. The HTP is measured in MLC 6260.

The chiral component C comprises one or more chiral compounds which have a mesogenic structure und exhibit preferably one or more mesophases themselves, particularly at least one cholesteric phase. Preferred chiral compounds being comprised in the chiral component C are, inter alia, well known chiral dopants like cholesteryl nonanoate (CN), R/S-811, R/S-1011, R/S-2011, R/S-3011, R/S-4011, R/S-5011, CB-15 (Merck KGaA, Darmstadt, Germany). Preferred are chiral dopants having one or more chiral moieties and one or more mesogenic groups or having one or more aromatic or alicyclic moieties forming, together with the chiral moiety, a mesogenic group. More preferred are chiral moieties and mesogenic chiral compounds disclosed in DE 34 25 503, DE 35 34 777, DE 35 34 778, DE 35 34 779, DE 35 34 780, DE 43 42 280, EP 01 038 941 and DE 195 41 820 that disclosure is incorporated herewithin by way of reference. Particular preference is given to chiral binaphthyl derivatives as disclosed in EP 01 111 954.2, chiral binaphtnol derivatives as disclosed in WO 02/34739, chiral TADDOL derivatives as disclosed in WO 02/06265 as well as chiral dopants having at least one fluorinated linker and one end chiral moiety or one central chiral moiety as disclosed in WO 02/06196 and WO 02/06195.

The controlling medium of the present invention has a characteristic temperature, preferably a clearing point, in the range from about −30° C. to about 80° C., especially up to about 55° C.

Preferred chiral compounds of the component C are selected from the group of the compounds C-I to C-III.

wherein

-   R^(a11), R^(a12), are each independently from each other alkyl,     oxalkyl, -   R^(a21), R^(a22) alkoxy or alkenyl with up 9 carbon atoms with the -   R^(a31) and R^(a32) provisos that     -   a) R^(a11)+R^(a12)     -   b) R^(a21)+R^(a22)

Preferably R^(a11), R^(a12), R^(a21), R^(a22), R^(a31) and R^(a32) are an alkyl group, especially a straight chain alkyl group.

Especially preferred are chiral binaphthyl derivates of the formulae C-IV,

Especially preferred are binaphthyl derivatives of the formulae C-IV-1a to IC-IV-1c,

-   Z⁰ is single bond, —CH₂CH₂—, —COO—, —OCO—, —CF₂O—, —OCF₂—, —CH₂O—,     —OCH₂—, —CF₂CF₂—, —CH═CH—, —C≡C— or —CF═CF—, -   b is 0, 1 or 2 -   R⁰* is hydrogen, an alkyl or alkoxy radical having from 1 to 15     carbon atoms wherein one or more methylene groups of said alkyl or     alkoxy radical may be replaced independetly of each other by —O—,     —S—, —SiR^(x)R^(y)—, —CH═CH—, —C≡C—, —CO—O— and/or —O—Cl— such that     oxygen and/or sulfur atoms are not linked directly to each other,     said alkyl or alkoxy radical being unsubstituted or mon- or     poly-substituted with halogen,

Furthermore chiral binaphthyl derivates ot the formulae C-V and C-VI are preferred

wherein

Z⁰ and b have the above given meanings and X is H, F, Cl, CN or has the meaning of R⁰*, R²* and R¹* are each independently is F, Cl, OCF₃, CF₃, CN and L¹, L², L³ and L⁴ are each H or F. Z⁰* denotes single bond, —C₂H₄—, —COO—, —OCO—, CH₂O—, —OCH₂—, —C₂F₄, —CH═CH—, —C≡C— or —CF═CF

Especially preferred are chiral binaphthyl derivatives of the formulae C-V-2a to C-V-2f:

The inventive mixtures contain one ore more (two, three, four or more) chiral compounds in the range of 1-25 wt. %, preferably 2-20 wt. %. Especially preferred are mixtures containing 3-15 wt. % of a chiral compound.

Preferred embodiments are indicated below:

-   The medium comprises one, two or more compounds of the formulae I; -   Componend B preferably contains beside at compounds of the formula     II at least one or more ester compounds of the formula Z -    where in R has the given meaning for R¹¹ -    X² is F, Cl, CN, NCS, OCF₃, CF₃ or SF₅.

Preferred compounds of the formula Z are

Especially preferred are mixtures containing 5-35 wt. %, preferably 10-30 wt. % and especially preferred 10-20 wt. %.

-   The component B contains additionally one or more compounds selected     from the group -   The medium component B additionally comprises one or more compounds     selected from the group consisting of the general formulae III to     VII:     in which the individual radicals have the following meanings:     -   R⁰ is n-alkyl, alkoxy, oxaalkyl, fluoroalkyl or alkenyl, each         having up to 9 carbon atoms,     -   X⁰ is CN, SF5, NCS, SO₂CF₃, F, Cl, halogenated alkyl,         halogenated alkenyl, halogenated alkenyloxy or halogenated         alkoxy having up to 6 carbon atoms,     -   Z⁰ is —C₂F₄—, —CF═CF—, —C₂H₄—, —(CH₂)₄—, —OCH₂—, —CH₂O—,         —CH═CH—, —CF₂O— or —OCF₂—, —C₂F₄—,     -   Y¹ to Y⁴ are each, independently of one another, H or F,     -   r is O or 1.

The compound of the formula V is preferably

-   The component B additionally comprises one or more compounds     selected from the group consisting of the general formulae VIII to     XV:     -   in which R⁰, X⁰ and y¹⁻⁴ are each, independently of one another,         as defined in claim 3. X⁰ is preferably F, Cl, CF₃, OCF₃ or         OCHF₂. R⁰ is preferably alkyl, oxaalkyl, fluoroalkyl or alkenyl,         each having up to 6 carbon atoms.

The component B additionally comprises one or more compounds of the formulae E-a to E-d

in which R⁰ is as defined in claim 3;

-   The proportion of the compounds of the formulae E-a to E-d is     preferably 10-30% by weight, in particular 15-25% by weight; -   The proportion of compounds of the formulae II to VII in the mixture     as a whole is from 1 to 30 weight; -   The medium comprises compounds of the formulae II, III, IV, V and/or     VI; -   R⁰ is straight-chain alkyl or alkenyl having from 2 to 7 carbon     atoms; -   Component B comprises further compounds, preferably selected from     the following group consisting of the general formulae XVI to XX:     -   in which R⁰ and X⁰ are as defined above. The 1,4-phenylene rings         may additionally be substituted by CN, chlorine or fluorine. The         1,4-phenylene rings are preferably monosubstituted or         polysubstituted by fluorine atoms. -   Liquid crystalline medium additionally comprises one, two, three or     more, preferably two or three, compounds of the formulae     -   in which “alkyl” and “alkyl*” are as defined below. The         proportion of the compounds of the formulae O1 and/or O2 in the         mixtures according to the invention is preferably 5-10% by         weight. -   The medium preferably comprises one, two or three compounds of the     formula IVa in which X⁰ is F or OCF₃. -   The medium preferably comprises one or more compounds of the     formulae IIa to IIg     -   in which R⁰ is as defined above. In the compounds of the         formulae IIa-IIg, R⁰ is preferably methyl, ethyl, n-propyl,         n-butyl or n-pentyl. -   The medium preferably comprises one or more compounds of the     formulae     -   in which R⁰ is as defined above. -   The proportion of the compounds of the formula lVb and/or IVc in     which X⁰ is fluorine and R⁰ is CH₃, C₂H₅, n-C₃H₇, n-C₄H₉ or     n-C₅H₁₁in the mixture as a whole is from 2 to 20% by weight, in     particular from 2 to 15% by weight. -   The medium preferably comprises compounds of the formulae II to VI     in which R⁰ is methyl.

The medium particularly preferably comprises compounds of the formulae

-   The medium preferably comprises one, two or more, preferably one or     two, dioxane compounds of the formulae -   The medium additionally comprises one, two or more bicyclic     compounds of the formulae Z1 to Z6     -   in which R^(1a) and R^(2a) are each, independently of one         another, H, CH₃, C₂H₅ or n-C₃H₇. R⁰, alkyl and alkyl* are as         defined in claim 3 or as defined below.

Of the said bicyclic compounds, particular preference is given to the compounds Z-1, Z-2, Z-5 and Z-6.

-   The medium additionally comprises one, two or more compounds having     fused rings, of the formulae AN1 to AN11:     -   in which R⁰ is as defined above.

It has been found that even a relatively small proportion of compounds of the formulae I mixed with conventional liquid-crystal materials, but in particular with one or more compounds of the formulae II, III, IV, V, VI and/or VII, results in a lower operating voltage and a broader operating temperature range. Preference is given, in particular, to mixtures which, besides one or more compounds of the formulae I, comprise one or more compounds of the formula II, in particular compounds of the formula II-5 and II-7 in which X¹² is F, Cl, CN, NCS, CF₃ or OCF₃. The compounds of the formulae I to VII are colourless, stable and readily miscible with one another and with other liquid-crystalline materials.

The term “alkyl” or “alkyl*” covers straight-chain and branched alkyl groups having 1-7 carbon atoms, in particular the straight-chain groups methyl, ethyl, propyl, butyl, pentyl, hexyl and heptyl. Groups having 1-5 carbon atoms are generally preferred.

The term “alkenyl” covers straight-chain and branched alkenyl groups having 2-7 carbon atoms, in particular the straight-chain groups. Preferred alkenyl groups are C₂-C₇-1E-alkenyl, C₄-C₇-3E-alkenyl, C₅-C₇-4-alkenyl, C₆-C₇-5-alkenyl and C₇-6-alkenyl, in particular C₂-C₇-1E-alkenyl, C₄-C₇-3E-alkenyl and C₅-C₇-4-alkenyl. Examples of particularly preferred alkenyl groups are vinyl, 1E-propenyl, 1E-butenyl, 1E-pentenyl, 1E-hexenyl, 1E-heptenyl, 3-butenyl, 3E-pentenyl, 3E-hexenyl, 3E-heptenyl, 4-pentenyl, 4Z-hexenyl, 4E-hexenyl, 4Z-heptenyl, 5-hexenyl, 6-heptenyl and the like. Groups having up to 5 carbon atoms are generally preferred.

The term “fluoroalkyl” preferably covers straight-chain groups having a terminal fluorine, i.e. fluoromethyl, 2-fluoroethyl, 3-fluoropropyl, 4-fluoro-butyl, 5-fluoropentyl, 6-fluorohexyl and 7-fluoroheptyl. However, other positions of the fluorine are not excluded.

The term “oxaalkyl” preferably covers straight-chain radicals of the formula C_(n)H_(2n+1)—O—(CH₂)_(m), in which n and m are each, independently of one another, from 1 to 6. Preferably, n=1 and m is from 1 to 6.

The optimum mixing ratio of the compounds of the formulae I and II+III+IV+V+VI+VII depends substantially on the desired properties, on the choice of the components of the formulae III, IV, V, VI and/or VII, and on the choice of any other components that may be present. Suitable mixing ratios within the range given above can easily be determined from case to case.

The total amount of compounds of the formulae I to XV in the mixtures according to the invention is not crucial. The mixtures can therefore comprise one or more further components for the purposes of optimisation of various properties. However, the observed effect on the operating voltage and the operating temperature range is generally greater, the higher the total concentration of compounds of the formulae I to XV.

In a particularly preferred embodiment, the media according to the invention comprise compounds of the formulae III to VII in which X⁰ is F, OCF₃, OCHF₂, OCH═CF₂, OCF═CF₂ or OCF₂—CF₂H. A favourable synergistic effect with the compounds of the formulae I results in particularly advantageous properties. In particular, mixtures comprising compounds of the formula I and of the formula II are distinguished by their low operating voltages.

The individual compounds of the formulae I to XX and their sub-formulae which can be used in the media according to the invention are either known or can be prepared analogously to the known compounds.

The construction of the MLC display according to the invention from polarisers, electrode base plates and surface-treated electrodes corresponds to the conventional construction for displays of this type. The term conventional construction is broadly drawn here and also covers all derivatives and modifications of the MLC display, in particular including matrix display elements based on poly-Si TFT or MIM.

A significant difference between the displays according to the invention and the conventional displays based on the twisted nematic cell consists, however, in the choice of the liquid-crystal parameters of the liquid-crystal layer.

The media according to the invention are prepared in a manner conventional per se. In general, the components are dissolved in one another, advantageously at elevated temperature. By means of suitable additives, the liquid-crystalline phases in accordance with the invention can be modified in such a way that they can be used in all types of liquid crystal display elements that have been disclosed hitherto. Additives of this type are known to the person skilled in the art and are described in detail in the literature (H. Kelker/R. Hatz, Handbook of Liquid Crystals, Verlag Chemie, Weinheim, 1980). For example, pleochroic dyes can be added for the preparation of coloured guest-host systems or substances can be added in order to modify the dielectric anisotropy, the viscosity and/or the alignment of the nematic phases. Furthermore, stabilisers and antioxidants can be added.

The mixtures according to the invention are suitable for TN, STN, ECB and IPS applications and isotropic switching mode (ISM) applications. Hence, there use in an electro-optical device and an electro-optical device containing liquid crystal media comprising at least one compound according to the invention are subject matters of the present invention.

The inventive mixtures are highly suitable for devices which operate in an optically isotropic state. The mixtures of the invention are surprisingly found to be highly suitable for the respective use.

Electro-optical devices that are operated or operable in an optically isotropic state recently have become of interest with respect to video, TV, and multi-media applications. This is because conventional liquid crystal displays utilizing electro-optical effects based on the physical properties of liquid crystals exhibit a rather high switching time which is undesired for said applications. Furthermore most of the conventional displays show a significant viewing angle dependence of contrast that in turn makes necessary measures to compensate this undesired property.

With regard to devices utilizing electro-optical effects in an isotropic state the German Patent Application DE 102 17 273 A1 for example discloses light controlling (light modulation) elements in which the mesogenic controlling medium for modulation is in the isotropic phase at the operating temperature. These light controlling elements have a very short switching time and a good viewing angle dependence of contrast. However, the driving or operating voltages of said elements are very often unsuitably high for some applicatons.

German Patent Application DE 102 41 301 yet unpublished describes specific structures of electrodes allowing a significant reduction of the driving voltages. However, these electrodes make the process of manufacturing the light controlling elements more complicated.

Furthermore, the light controlling elements, for example, disclosed in both DE 102 17 273 A1 and DE 102 41 301 show a significant temperature dependence. The electro-optical effect that can be induced by the electrical field in the controlling medium being in an optical isotropic state is most pronounced at temperatures close to the clearing point of the controlling medium. In this range the light controlling elements have the lowest values of their characteristic voltages and, thus, require the lowest operating voltages. As temperature increases the characteristic voltages and hence the operating voltages increase remarkably. Typical values of the temperature dependence are in the range from about a few volts per centigrade up to about ten or more volts per centigrade. While DE 102 41 301 describes various structures of electrodes for devices operable or operated in the isotropic state, DE 102 17 273 A1 discloses isotropic media of varying composition that are useful in light controlling elements operable or operated in the isotropic state. The relative temperature dependence of the threshold voltage in these light controlling elements is at a temperature of 1 centigrade above the clearing point in the range of about 50%/centigrade. That temperature dependence decreases with increasing temperature so that it is at a temperature of 5 centigrade above the clearing point of about 10%/centigrade. However, for many practical applications of displays utilizing said light controlling elements the temperature dependence of the electro-optical effect is too high. To the contrary, for practical uses it is desired that the operating voltages are independent from the operating temperature over a temperature range of at least some centigrades, preferably of about 5 centigrades or more, even more preferably of about 10 centigrades or more and especially of about 20 centigrades or more.

Now it has been found that the use of the inventive mixtures are highly suitable as controlling media in the light controlling elements as described above and in DE 102 17 273 A1, DE 102 41 301 and DE 102 536 06 and broaden the temperature range in which the operating voltages of said electro-optical operates. In this case the optical isotropic state or the blue phase is almost completely or completely independent from the operating temperature.

This effect is even more distinct if the mesogenic controlling media exhibit at least one so-called “blue phase” as described in yet unpublished DE 103 13 979. Liquid crystals having an extremely high chiral twist may have one or more optically isotropic phases. If they have a respective cholesteric pitch, these phases might appear bluish in a cell having a sufficiently large cell gap. Those phases are therefore also called “blue phases” (Gray and Goodby, “Smectic Liquid Crystals, Textures and Structures”, Leonhard Hill, USA, Canada (1984)). Effects of electrical fields on liquid crystals existing in a blue phase are described for instance in H. S. Kitzerow, “The Effect of Electric Fields on Blue Phases” , Mol. Cryst. Liq. Cryst. (1991), Vol. 202, p. 51-83, as well as the three types of blue phases identified so far, namely BP I, BP II, and BP III, that may be observed in field-free liquid crystals. It is noteworthy, that if the liquid crystal exhibiting a blue phase or blue phases is subjected to an electrical field, further blue phases or other phases different from the blue phases I, II and III might appear.

The inventive mixtures can be used in an electro-optical light controlling element which comprises

-   one or more, especially two substrates; -   an assembly of electrodes; -   one or more elements for polarizing the light; and -   said controlling medium;     whereby said light controlling element is operated (or operable) at     a temperature at which the controlling medium is in an optically     isotropic phase when it is in a non-driven state.

The controlling medium of the present invention has a characteristic temperature, preferably a clearing point, in the range from about −30° C. to about 8020 C., especially up to about 5520 C.

The operating temperature of the light controlling elements is preferably above the characteristic temperature of the controlling medium said temperature being usually the transition temperature of the controlling medium to the blue phase; generally the operating temperature is in the range of about 0.1° to about 50°, preferably in the range of about 0.1° to about 10° above said characteristic temperature. It is highly preferred that the operating temperature is in the range from the transition temperature of the controlling medium to the blue phase up to the transition temperature of the controlling medium to the isotropic phase which is the clearing point. The light controlling elements, however, may also be operated at temperatures at which the controlling medium is in the isotropic phase.

(For the purposes of the present invention the term “characteristic temperature” is defined as follows:

-   If the characteristic voltage as a function of temperature has a     minimum, the temperature at this minimum is denoted as     characteristic temperature. -   If the characteristic voltage as a function of temperature has no     minimum and if the controlling medium has one or more blue phases,     the transistion temperature to the blue phase is denoted as     characteristic temperature; in case there are more than one blue     phase, the lowest transition temperature to a blue phase is denoted     as characteristic temperature. -   If the characteristic voltage as a function of temperature has no     minimum and if the controlling medium has no blue phase, the     transistion temperature to the isotropic phase is denoted as     characteristic temperature.)

In the context of the present invention the term “alkyl” means—as long as it is not defined in a different manner elsewhere in this description or in the claims—straight-chain and branched hydrocarbon (aliphatic) radicals with 1 to 15 carbon atoms. The hydrocarbon radicals may be unsubstituted or substituted with one or more substituents being independently selected from the group consisting of F, Cl, Br, I or CN.

The dielectrics may also comprise further additives known to the person skilled in the art and described in the literature. For example, 0-15% of pleochroic dyes, antioxidants or stabilizers can be added.

C denotes a crystalline phase, S a smectic phase, S_(C) a smectic C phase, N a nematic phase, I the isotropic phase and BP the blue phase.

V₁₀ denotes the voltage for 10% transmission, V100 denotes the voltage for 100% transmission (viewing angle perpendicular to the plate surface). t_(on) denotes the switch-on time and t_(off) the switch-off time at an operating voltage corresponding the value of V100.

Δn denotes the optical anisotropy. Δ∈ denotes the dielectric anisotropy (Δ∈=∈_(∥)−∈_(⊥), where ∈_(∥)denotes the dielectric constant parallel to the longitudinal molecular axes and ∈_(⊥)denotes the dielectric constant perpendicular thereto). The electro-optical data are measured in a TN cell at the 1st minimum (i.e. at a d·Δn value of 0.5 μm) at 20° C., unless expressly stated otherwise. The optical data are measured at 20° C., unless expressly stated otherwise.

In the present application and in the examples below, the structures of the liquid-crystal compounds are indicated by means of acronyms, the transformation into chemical formulae taking place in accordance with Tables A and B below. All radicals C_(n)H_(2n+1) and C_(m)H_(2m+1) are straight-chain alkyl radicals having n and m carbon atoms respectively; n and m are integers and are preferably 0, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11 or 12. The coding in Table B is self-evident. In Table A, only the acronym for the parent structure is indicated. In individual cases, the acronym for the parent structure is followed, separated by a dash, by a code for the substituents R¹*, R²*, L¹* and L²*: Code for R¹*, R²*, L¹*, L²* R¹* R²* L¹* L²* nm C_(n)H_(2n+1) C_(m)H_(2m+1) H H nOm OC_(n)H_(2n+1) C_(m)H_(2m+1) H H nO.m C_(n)H_(2n+1) OC_(m)H_(2m+1) H H n C_(n)H_(2n+1) CN H H nN.F C_(n)H_(2n+1) CN F H nN.F.F C_(n)H_(2n+1) CN F F nF C_(n)H_(2n+1) F H H nCl C_(n)H_(2n+1) Cl H H nOF OC_(n)H_(2n+1) F H H nF.F C_(n)H_(2n+1) F F H nF.F.F C_(n)H_(2n+1) F F F nmF C_(n)H_(2n+1) C_(m)H_(2m+1) F H nOCF₃ C_(n)H_(2n+1) OCF₃ H H nOCF₃.F C_(n)H_(2n+1) OCF₃ F H n-S C_(n)H_(2n+1) NCS H H n-Vm C_(n)H_(2n+1) —CH═CH—C_(m)H_(2m+1) H H nV-Vm C_(n)H_(2n+1)—CH═CH— —CH═CH—C_(m)H_(2m+1) H H

Preferred mixture components are given in Tables A and B. TABLE A

TABLE B

Particular preference is given to liquid-crystalline mixtures which, besides the compounds of the formula I, comprise at least one, two, three or four compounds from Table B. TABLE C Table C shows possible dopants according to component C which are generally added to the mixtures alone or in combination two, three or more) according to the invention.

TABLE D Stabilisers which can be added, for example, to the mixtures according to the invention are mentioned below.

EXAMPLES

The following examples are intended to explain the invention without restricting it. Above and below, percentages are per cent by weight. All temperatures are given in degrees Celsius. m.p. denotes melting point, cl.p. clearing point. Furthermore, C=crystalline state, N=nematic phase, S=smectic phase, I=isotropic phase. T_(Trans)=transition temperature from cholesteric to blue phase (BP).

The medium is introduced into a test cell with interdigital electrodes on one substrate only. The thickness of the mesogenic layer in the cell is 10 μm and the distance between the electrodes is 10 μm, the electrode width is 10 μm.

The data between these symbols represent the transition temperatures. An denotes optical anisotropy (589 nm, 20° C.). The flow viscosity ν₂₀ (mm²/sec) and the rotational viscosity γ₁ (mPa·s) were each determined at 20° C.

The physical data illustrate which properties can be achieved in which ranges.

The “usable range” is determined by switching times being smaller than 5 msec within this temperature range.

Examples Example 1

AGUQU-2-F 9.90% T_(trans) [° C.]: 12.0 AGUQU-3-F 4.50% Blue Phase range [K]: 10.0 AUUQU-3-F 11.70% useable range [K): 7.0 AUUQU-3-T 11.70% CUUQU-2-OT 12.60% CUUQU-3-OT 12.60% PUZU-5-F 10.80% PUQU-2-F 7.20% PUQU-3-F 9.00% R-5011 5.00% IS-11480 5.00%

Example 2

AUUQU-3-N 10.00% CUZP-3N.F.F 9.00% GZU-3A-N 9.00% AUUQU-3-OT 10.00% AUUQU-3-F 9.00% AUUQU-3-T 8.00% AUUQP-3-T 4.00% PUZU-3-F 9.00% PUZU-5-F 8.00% PUQU-2-F 9.00% IS-11480 10.00% R-5011 5.00%

Example 3

AUUQU-3-N 10.00% T_(trans) [° C.]: 73.5 AUZU-3-N 10.00% CUZP-4N.F.F 9.00% GZU-3A-N 8.00% GZU-4A-N 5.00% HP-3N.F 8.00% AUUQU-3-OT 9.50% AUUQU-3-T 8.00% AUUQPU-3-F 7.00% AUUQGU-3-F 8.00% IS-11480 12.50% R-5011 5.00%

Example 4

AUUQU-3-N 10.00% T_(trans) [° C.]: 38.0 AUZU-3-N 10.00% Blue Phase range [K]: 13.0 CUZP-4N.F.F 9.00% GZU-3A-N 8.00% HP-3N.F 8.00% HP-5N.F 3.00% AUUQU-3-OT 10.00% AUUQU-3-T 8.00% AUUQU-3-F 9.00% AUUQGU-3-F 8.00% IS-11480 10.00% R-5011 7.00%

Example 5

AUUQU-3-N 10.00% T_(trans) [° C.]: 66.0 AUZU-3-N 10.00% CUZP-4N.F.F 9.00% GZU-3A-N 8.00% GZU-4A-N 3.00% HP-3N.F 8.00% HP-5N.F 8.00% AUUQU-3-T 7.00% AUUQPU-3-F 7.00% AUUQGU-3-F 8.00% IS-11480 15.00% R-5011 7.00%

Example 6

AUUQU-3-N 10.00% T_(trans) [° C.]: 31.0 AUZU-3-N 10.00% Blue Phase range [K]: 16.5 AUZU-5-N 10.00% useable range [K): 13.0 GZU-3A-N 8.00% HP-3N.F 6.00% AUUQU-3-OT 10.00% AUUQU-3-T 8.00% AUUQU-3-F 9.00% AUUQGU-3-F 8.00% PUZU-3-F 7.00% IS-11480 7.00% R-5011 7.00%

Example 7

UZU-4A-N 6.00% T_(trans) [° C.]: −2.5 UZU-5A-N 6.00% GZU-3A-N 6.00% GZU-4A-N 6.00% AUUQU-3-OT 9.00% AUUQU-3-F 8.00% AUUQU-3-T 8.00% AGUQU-3-F 2.00% PUZU-3-F 8.00% PUZU-5-F 8.00% AUZU-3-N 8.00% AUZU-5-N 8.00% IS-11489 10.00% IS-11663 7.00%

Example 8

AUUQU-3-N 10.092% T_(trans) [° C.]: 31.0 AUZU-3-N 10.092% Blue Phase range [K]: 17.0 AUZU-5-N 10.092% useable range [K): 13.0 GZU-3A-N 8.091% HP-3N.F 6.090% AUUQU-3-OT 10.092% AUUQU-3-T 8.091% AUUQU-3-F 9.135% AUUQGU-3-F 8.091% PUZU-3-F 7.134% R-5011 8.000% IS-11480 5.000%

Example 9

R-5011 9.00% T_(trans) [° C.]: 20.6 IS-11480 5.00% Blue Phase range [K]: 20.0 AUUQU-3-N 9.98% useable range [K): 15.0 AUZU-3-N 9.98% AUZU-5-N 9.98% GZU-3A-N 8.00% HP-3N.F 6.02% AUUQU-3OT 9.98% AUUQU-3-T 8.00% AUUQU-3-F 9.03% AUUQGU-3-F 8.00% PUZU-3-F 7.05%

Example 10

R-5011 9.00% IS-11489 5.00% AUUQU-3-N 9.98% AUZU-3-N 9.98% AUZU-5-N 9.98% GZU-3A-N 8.00% HP-3N.F 6.02% AUUQU-3-OT 9.98% AUUQU-3-T 8.00% AUUQU-3-F 9.03% AUUQGU-3-F 8.00% PUZU-3-F 7.05%

Example 1 1

AUUQU-3-N 9.976% AUZU-3-N 9.976% AUZU-5-N 9.976% GZU-3A-N 7.998% HP-3N.F 6.020% AUUQU-3-OT 9.976% AUUQU-3-T 7.998% AUUQU-3-F 9.030% AUUQGU-3-F 7.998% PUZU-3-F 7.052% R-5011 2.000% IS-11480 12.000%

Example 12

R-5011 5.00% T_(trans) [° C.]: 22.5 IS-11851 10.00% Blue Phase range [K]: 6.0 GZU-40-N 6.80% AUUQU-3-N 10.20% AUZU-3-N 10.20% CUZP-4N.F.F 10.20% GZU-3A-N 8.50% GZU-4A-N 8.50% HP-3N.F 3.40% HP-5N.F 3.40% AUUQU-3-T 6.80% AUUQPU-3-F 5.10% AUUQGU-3-F 5.10% UZU-3A-N 6.80% 

1. Liquid-crystalline medium comprising a) 1-25% by weight of a component A containing at least one compound of the formula I

 wherein a, b, c and d are each independently of each other 0, 1 or 2, whereby a+b+c+d≦4; R¹¹ is an alkyl or alkoxy radical having from 1 to 15 carbon atoms, wherein one or more methylene groups of said alkyl or alkoxy radical may be replaced independently of each other by —O—, —S—, —SiR^(x)R^(y)—, —CH═CH—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not linked directly to each other, said alkyl or alkoxy radical being unsubstituted or mono-substituted with a —CN group or mono- or poly-substituted with halogen, L¹¹, L¹², L¹³ and L¹⁴ are each independently of each other hydrogen, halogen, a CN group, an alkyl or alkoxy radical having from 1 to 15 carbon atoms wherein one or more methylene groups of said alkyl or alkoxy radical may be replaced independently of each other by —O—, —S—, —SiR^(x)R^(y)—, —CH═CH—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not linked directly to each other, said alkyl or alkoxy radical being unsubstituted or mono-substituted with a —CN group or mono- or poly-substituted with halogen, with the proviso that at least one of L¹¹, L¹², L¹³ and L¹⁴ is not hydrogen, X¹¹ is halogen, —CN, —NCS, —SF₅, S—R^(Z), —SO₂—R^(Z), an alkyl or alkoxy radical having from 1 to 15 carbon atoms, wherein one or more methylene groups of said alkyl or alkoxy radical may be replaced independently of each other by —O—, —S—, —SiR^(x)R^(y)—, —CH═CH—, —C≡C—, —CO—O— and/or —O—CO— such that oxygen and/or sulfur atoms are not linked directly to each other, said alkyl or alkoxy radical being unsubstituted or mono- substituted with a —CN group or mono- or poly-substituted with halogen; R^(x) and R^(y) are each independently of each other hydrogen or an alkyl radical having from 1 to 7 carbon atoms; R^(Z) is an alkyl radical having from 1 to 7 carbon atoms, said alkyl radical being unsubstituted or mono- or poly-substituted with halogen; A¹¹, A¹², A¹³ and A¹⁴ are each independently of each other a ring of one of the following formulas:

 whereby each of A¹¹, A¹², A¹³ and A¹⁴ may be the same ring or two different rings if present twice; Y¹¹, Y¹², Y¹³ and Y¹⁴ are each independently of each other hydrogen, halogen, CN, an alkyl or alkoxy radical having from 1 to 15 carbon atoms wherein one or more methylene groups of said alkyl or alkoxy radical may be replaced independently of each other by —O—, —S—, —SiR^(x)R^(y)—, —CH═CH—, —C≡C—, —CO—O— and/or —O—CO—such that oxygen and/or sulfur atoms are not linked directly to each other, said alkyl or alkoxy radical being unsubstituted or mono- or poly-substituted with halogen, f, g and h are each independently of each other 0, 1, 2 or 3; Z¹¹, Z¹², Z¹³ and Z¹⁴ are independently of each other a single bond, —(CH₂)₄)—, —CH₂CH₂—, —CF₂—CF₂—, —CF₂—CH₂—, —CH₂—CF₂—, —CH═CH—, —CF═CF—, —CF═CH—, —(CH₂)₃O—, —O(CH₂)₃—, —CH═CF—, —C≡C—, —CH₂O—, —OCH₂—, —CF₂O—, —OCF₂—, —CO—O— or —O—CO— whereby each of Z¹¹, Z¹², Z¹³ and Z¹⁴ may have the same or a different meaning if present twice; b) 5-80% by weight of a component B containing at least one compound of the formula II

 wherein R¹² has the meaning given for R¹¹ A¹, A², A³ are each independently of each other

Z¹ and Z² are independently of each other a single bond, —(CH₂)₄)—, —CH₂CH₂—, —CF₂—CF₂—, —CF₂—CH₂—, —CH₂—CF₂—, —CH═CH—, —CF═CF—, —CF═CH—, —(CH₂)₃O—, —O(CH₂)₃—, —CH═CF—, —C≡C—, —CH₂O—, —OCH₂—, —CF₂O—, —OCF₂—, —CO—O— or —O—CO— whereby each of Z¹¹, Z¹², Z¹³ and Z¹⁴ may have the same or a different meaning if present twice; X¹² is halogen, —CN, —NCS, —SF₅, —SO₂CF₃, alkyl, alkenyl, alkenyloxy or alkylalkoxy or alkoxy ratical each mono- or polysubstituted by CN and/or halogen, L¹ and L² are each independently of each other H or F, and m and n are each independently of each other 0, 1, or 2 and m+n≦2; and c) optionally 1-20% by weight of component C containing at least one chiral compound with a HTP of ≧20 μm.
 2. Liquid-crystalline medium according to claim 1, characterized in that it comprises one or more compounds of formula I wherein at least one of L¹¹ to L¹⁴ is alkoxy.
 3. Liquid-crystalline medium according to claim 2, characterized in that it comprises one or more compounds of formula I wherein at least two of L¹¹ to L¹⁴ are alkoxy.
 4. Liquid-crystalline medium according to at least one of claims 1 to 3, characterized in that it comprises 1-20% of component C.
 5. Liquid-crystalline medium according to at least one of claims 1 to 4, characterized in that it comprises one, two or more compounds of the formulae II-1 to II-8:


6. Use of the liquid-crystalline medium according to at least one of claims 1 to 5 in an electro-optical device.
 7. Electro-optical device characterized in that it contains the liquid crystal medium according to at least one of claims 1 to
 5. 8. Use of the liquid crystal medium according to at least one of claims 1 to 5 in an electro-optical device said device being operated or being operable in an optically isotropic state. 